Open Access. Powered by Scholars. Published by Universities.®
Articles 1 - 4 of 4
Full-Text Articles in Engineering
Modifying Casting Parameters To Improve The High Temperature Ductility Of Investment Cast Nickel-Based Superalloy Pwa 1455, Lars Alexander Hedin, Cole Magnum Introligator
Modifying Casting Parameters To Improve The High Temperature Ductility Of Investment Cast Nickel-Based Superalloy Pwa 1455, Lars Alexander Hedin, Cole Magnum Introligator
Materials Engineering
PCC Structurals, an industry leader in superalloy investment castings, has observed inconsistencies in the stress rupture performance of polycrystalline nickel-based superalloy PWA 1455. PCC has changed their casting parameters to reduce the thermal gradient during cooling but have been unable to correlate these changes with an increase in stress rupture elongation. Metallographic examination of past samples indicated microstructures composed of non- equiaxed dendritic grains with mean diameter of .021 inches along the test axis. A similar study on polycrystalline superalloys has indicated that excessive superheat temperatures above the liquidus can result in large grains identical to those observed, limiting the …
Kinked Tensile Behavior Of Cold Worked Nitinol, Grant R. Caraway, Samuel J. Canovas
Kinked Tensile Behavior Of Cold Worked Nitinol, Grant R. Caraway, Samuel J. Canovas
Materials Engineering
To characterize the decrease in ductility caused by an induced stress concentration as a function of various levels of cold work and heat treatment, Nitinol medical guide wires with a .004″ diameter were tested using both a standard, straight tensile test and a modified, bent tensile test. The ratio of the two break loads (bent:straight) for identically processed samples was used as a proxy for measuring the ductility of the guide wires: the higher the ratio, the more ductile the sample. The average break load ratio as a function of increased cold work, decreased from 1.27 to 0.91 for the …
Effects Of Cold Work, Final Grind Diameter, And Heat Treatment On The Mechanical Properties Of Nitinol Guide Wire Tips, Daniel Rodriguez
Effects Of Cold Work, Final Grind Diameter, And Heat Treatment On The Mechanical Properties Of Nitinol Guide Wire Tips, Daniel Rodriguez
Materials Engineering
No abstract provided.
Controlling Grain Size In Cold Worked And Annealed 1100 Aluminum To Optimize Ductility In Rocket Diaphragm Systems, Ryan Lewis, Bryce Simmons, Jessica Williams
Controlling Grain Size In Cold Worked And Annealed 1100 Aluminum To Optimize Ductility In Rocket Diaphragm Systems, Ryan Lewis, Bryce Simmons, Jessica Williams
Materials Engineering
Liquid propellant rocket diaphragms require extreme ductility. 1100 Aluminum is used for its high ductility, but the post-processing cold work and subsequent anneal result in excessively large grains. The effect of heat treatment and cold work on grain size in 1100 aluminum was explored. The samples were cold worked to 0, 5, 10, 15 and 30% using tensile elongation. The samples were then heat treated per AMS 2770 with either a "Steel Conduction" (1000 – 1150°F/min) or a "Production" (16 – 18°F/min) heating rate. The grain size of the samples were measured using the mean lineal intercept method. The grain …