Effects Of Composition And Solid Solution Strengthening On The Compression Strength Of Iron-Based Hardfacing Alloys, Tyler Wiggins, Samuel Garrison-Terry

Materials Engineering

Three iron-based hardfacing alloys were fabricated to have a tungsten strengthened matrix with varying compositions of 10-15, 20, and 30 wt% tungsten/chrome boride content. The fourth sample was fabricated to have a molybdenum solid solution strengthened matrix with 10-15 wt% W/Cr Boride content. This project focuses on the compressive strength of iron-based hardfacing alloys. Preliminary compression tests with Scoperta iron-based hardfacing alloys showed a need for sample dimension reduction due to compressive loads that could not be met by a 50 kN maximum capacity mechanical testing system. The preliminary tests showed compressive strengths exceeding 2340 MPa. Samples of the current …