Engineering Commons^™

Laser Ablation Of Silicon Surfaces : The Effects Of A Low Level Background Light, Taposh Kumar Gayen

Theses

The performance of high speed optoelectronic and microelectronic devices largely depends on the uniqueness and development of the fabrication technology. Laser ablation has proven to be an effective three dimensional surface patterning technology. In this thesis, we present findings on the patterning of semiconductor surfaces using laser ablation in air as well as in solutions.

In this thesis, we suggest that the depth of a pattern induced on silicon by firing a pulsed excimer laser in air varies almost linearly with the number of pulses. We report that a He-Ne laser as a background light source has virtually little or …

Synthesis And Characterization Of Silicon Nitride Films Deposited By Plasma Enhanced Chemical Vapor Deposition Using Diethylsilane, Yanyao Yu

Theses

Silicon nitride thin films were deposited on silicon substrates using Diethylsilane (DES) and ammonia by Plasma Enhanced Chemical Vapor Deposition (PECVD) over a temperature range of 100 - 300°C, a pressure range of 0.2 - 0.6 torr, and a ratio of NH₃/DES was varied from 6 - 26. The R.F. power and frequency were kept at 0.15 watts/cm^{2 and 100 KHz respectively. DES flow rate was set at 15 sccm for all experiments in this study. One set of experiments were performed at different values of one parameter while the other parameters were kept constant.}

The deposition …

Synthesis And Characterization Of Lpcvd Boron Nitride Films For X-Ray Lithography, Wen-Pin Kuo

Theses

Boron nitride thin films were deposited on silicon and fused quartz substrates using ammonia and the liquid precursor borane-triethylamine complex (TEAB) by low pressure chemical vapor deposition over a temperature range of 300-850°C, a pressure range of 0.21-0.6 torr, and an ammonia flow rate range of 0-740 sccm. An increased in the nitrogen content in the film due to the addition of ammonia flow resulted in a pronounced improvement in the optical transmission, an increase in the film uniformity and a decrease in the depletion effect. IR spectra of the films showed an asymmetrical wide band centered around 1400 cm …