The Morphology Of Uhmwpe Wear Debris Generated By A Hip Joint Simulator, Aaron P. Essner

Theses

The size, quantity and shape of total hip replacement wear debris may identify wear mechanisms as well as play a role in osteolysis. Characterization of wear particles generated from a hip joint simulator was conducted followed by comparison with literature reported in vivo results. The effect of counterface material and lubricant type on particle morphology was assessed. Biomaterial pairs including UHMWPE articulated against CoCr, Alumina and Zirconia were considered. Deionized (D.I.) water and bovine serum were used as lubricants. Particles generated from Alumina/UHMWPE in serum were slightly larger than those for CoCr and Zirconia against UHMWPE in serum. Particle shape …

An Experimental Investigation Of Wear Behavior Of Ultra-High Molecular Weight Polyethylene Under Sliding Motion, Elham Zand-Moghaddam

Theses

This project investigates the effect of sliding motion on the materials that are used as bearing surfaces of human total-joint replacement prostheses.

The tests are performed with a specially designed equipment based on pin-on-disk machine. The testing machine is designed and constructed to reproduce sliding motion, applied to spherical ended metal "Canine-Head" components such as dog hip acting on a flat polyethylene surface. The sliding motion is performed by applying different constant loads for 5,000,000 cycles. The tests are carried out with the wear specimen lubricated by deionized water.

The purpose is to produce delamination, which is the severe wear …