High Cycle Rotating Bending Fatigue Of 6061-T6 Friction Stir Welded Extrusions, John Chang, Travis Miller

Materials Engineering

Fatigue testing was done on friction stir welded joints of 6061-T6 aluminum extrusions. Tests were run using a rotating bending fatigue machine at stresses from 111.5 to 138.7 MPa. Failures occurred on the order of 10⁵ to 10⁷ cycles, and an S-N curve was generated based off of the failure results. After the samples failed, the location of the failure and the number of cycles to failure were noted. Fatigue samples were designed in SolidWorks with a tapered 2 inch reduced section. The 2 inch reduced section will include the entire weld region as seen from the microhardness …