Full-Text Articles in Engineering
Characterization Of Aluminum-Boron Carbide Particulate Metal Matrix Composites, Eric Blank
Characterization Of Aluminum-Boron Carbide Particulate Metal Matrix Composites, Eric Blank
Materials Engineering
The analysis of die-cast 380 aluminum-boron carbide particulate metal matrix composites (MMC) was performed in order to see if the samples had the required tensile strength of 300 MPa. 10wt% B4C die-cast samples were produced and tested. Half were heat treated to the T6 condition and the others were left as cast. Using ASTM standard B 557M it was found that the average tensile strength for the as-cast samples was 130 MPa and the heat treated samples had a tensile strength of 93 MPa. These values were both lower than expected. The heat treated samples were not expected to have …
Validation Of A Secondary Fabric Supplier And Characterization Of Alternate Cores For Use In The Aptera 2e Sandwich Core Composite, Bryan Rogers
Materials Engineering
Polymer matrix composites’ high strength to weight ratio has made them an ideal material choice for use in lightweight transportation vehicles. Aptera Motors, a company based out of Oceanside, CA, is currently developing a next-generation high efficiency passenger vehicle called the Aptera 2e. The 2e’s body is composed of a sandwich core composite containing laminates of E-glass fibers embedded within an epoxy matrix sandwiched between a polyester hexagonal core. This project looked to validate a secondary fabric supplier for use in Aptera’s composite and characterize the core shear properties of two alternate core materials for future iterations of Aptera’s vehicle. …