Characterization And Analysis Of Low Room Temperature Ductility Nickel-Based Superalloy 718 Plus For Aircraft Engine Forgings, Jonathon Bracci
Characterization And Analysis Of Low Room Temperature Ductility Nickel-Based Superalloy 718 Plus For Aircraft Engine Forgings, Jonathon Bracci
Materials Engineering
Schlosser Forge Co. forges low pressure turbine (LPT) cases from the nickel based superalloy 718 Plus using the ring rolling forging process. Schlosser has been experiencing low room temperature ductility problems in a number of their 718 Plus LPT cases. LPT cases are required to pass a 4D tensile test at room temperature with a minimum of 15 percent elongation. The ductility problem was reduced by increasing the forging temperature from 1825˚F to 1850˚F. Analysis was performed on 718 Plus samples taken from forged LPT cases that failed the room temperature ductility requirement and ones that passed the requirement. The …
Effect Of Heating Temperature, Heating Time And Initial Microstructure On Recrystallization Of Waspaloy During Heating For Forging, Marissa Hill
Materials Engineering
A fine, uniform grain size is required for creep limited Waspaloy in aircraft engine applications. Upon heating, Waspaloy does not always recrystallize in a uniform manner resulting in occasional large grains with a majority of the grains meeting the grain size requirements. Waspaloy’s microstructure was analyzed with different heat treatments and in the as-forged condition. The strengthening mechanism is the gamma prime phase. The gamma prime solvus temperature is 1908°F so the different heat treatments were determined around that temperature, as well as the forging temperature range of 1800-2150°F. At the 1850°F heat treatment, the microstructure recrystallized with small grains, …
Microstructural Characterization Of Ti-6al-4v And Its Relationship To Sample Geometry, Blake Gaspar
Microstructural Characterization Of Ti-6al-4v And Its Relationship To Sample Geometry, Blake Gaspar
Materials Engineering
A problem exists with a part produced by forging made by Shultz Steel of Ti-6Al-4V in the variance of properties throughout the part. There is one specific region that exhibits the most variance. The purpose of the report is to determine any microstructural differences within the region of interest in the part. When microstructures of the inner section and outer section of the part were looked at it was determined that they exhibited a martensitic structure. There was a noticeable difference in the lath structure between sections. The outer region contained larger more widely spread laths of an average length …
Analysis Of Failed Forging Saddling Mandrels And Process Improvements For Increased Mandrel Lifespan, Brock Costalupes
Analysis Of Failed Forging Saddling Mandrels And Process Improvements For Increased Mandrel Lifespan, Brock Costalupes
Materials Engineering
This project seeks to increase the lifespan of steel mandrels used by Schlosser Forge in the saddling process, which is part of the production of forged rings for the aerospace and power generation industries. All saddle mandrel samples were taken from used 4340 steel mandrels. Hardness profiles were measured across rectangular bars cut from the transverse direction of a completely fractured piece of a 7″ diameter mandrel. The hardness near one outer surface of the tested bar was 36 HRC and gradually decreased to 30.5 HRC at the opposite surface. Macroscopic examination of the primary fracture surface along with light …
Effects Of Annealing/Solution Treating And Aging On Longitudinal And Transverse Properties Of Ti-6al-4v Forgings, Blake Reller
Effects Of Annealing/Solution Treating And Aging On Longitudinal And Transverse Properties Of Ti-6al-4v Forgings, Blake Reller
Materials Engineering
Forty-eight subsize round-bar tensile samples (ASTM E8) were machined from 3-in-thick forgings of Ti-6Al-4V. Half of these samples were cut so the axis aligned with the longitudinal (LG) direction of the forging, the other half were cut to align with the transverse (LT) direction. Four samples from each direction were subjected to one of six heat treatments so that a total of eight samples received each treatment. Annealed samples were held at 1350°F for two hours, then air cooled. Solution treated and aged (STA) samples were solution treated at one of five temperatures between 1785°F and 1435°F for one hour …
Characterization Of Positive Macrosegregation At The Subsurface Of Direct-Chill Cast 7050 Aluminum Forging Billets, Aaron Youril
Characterization Of Positive Macrosegregation At The Subsurface Of Direct-Chill Cast 7050 Aluminum Forging Billets, Aaron Youril
Materials Engineering
Segregation of alloying elements during casting of forging billets may persist to the final forged component leading to unacceptable surface appearance. Determination of the elements or compounds that segregate is the essential first step to solving this problem. Differential Scanning Calorimetry (DSC) was used to determine a composition profile of the macrosegregation occurring at the subsurface of an as-cast 7050 aluminum alloy billet. Data collection was carried out by separating 10 to 20 mg samples from the outer centimeter along the radius of the billet, as well as samples from the bulk interior of the billet for comparison with the …