Characterization And Mechanical Properties Of Α-Al2o3 Particle Reinforced Aluminium Matrix Composites, Synthesized Via Uniball Magneto-Milling And Uniaxial Hot Pressing, Buraq Talib Shalash Al-Mosawi, David Wexler, Andrzej Calka

Faculty of Engineering and Information Sciences - Papers: Part A

Al-based composite powders containing 2, 4, 7 and 10 volume fraction of α-Al₂O₃ were prepared using the uniball controlled magneto-milling method and were then uniaxially hot pressed at (600 ± 10)°C under 70 MPa for 15 min. The resulting composites were greater than 99% theoretical density with enhanced mechanical properties. Detailed characterization was performed using: X-ray diffraction, scanning electron microscopy equipped with energy dispersive spectroscopy, electrical conductivity, compression, ultra-micro indentation testing and pin on drum wear testing at ambient temperature. Microstructure-mechanical property correlations were obtained as functions of α-Al₂O₃ volume fraction. It was found …