Ceramic Dielectrics For High Energy Density Capacity Application, Sheng Chao
Ceramic Dielectrics For High Energy Density Capacity Application, Sheng Chao
Doctoral Dissertations
"The objective of this dissertation is to investigate the relationship between the processing parameters, microstructural development, defect chemistry and electrical properties of titanium oxide (TiO₂) dielectrics for high energy density capacitor applications. The effects of aliovalent dopants on the dielectric properties of TiO₂ ceramics were investigated, aiming to further improve the desired dielectric properties especially at elevated temperatures (up to 200°C). Due to the segregation of acceptor type impurities in the starting powders, space charge polarization took place in TiO₂ ceramics with relative large grain size (>̲500nm), leading to high dielectric loss and low energy storage efficiency. Increased ratio …
Phase Equilibria In Iron Phosphate System, Liying Zhang
Phase Equilibria In Iron Phosphate System, Liying Zhang
Doctoral Dissertations
"The main objectives of this research were to synthesize iron phosphate compounds, study phase equilibria in the iron phosphate system, focusing on the glass forming area, and investigate glass formability and properties based on the liquidus regions. Twelve iron phosphate compounds were successfully prepared and studied in terms of liquidus temperature or decomposition behavior. The liquidus surface of the Fe₃PO₇- Fe(PO₃)₃ system was re-determined and found to be significantly different from that originally presented by Wentrup in 1935. Eutectic points exist at 58.0 mole% Fe₂O₃ (1070⁰C), 42.7 mole% Fe₂O₃ (925°C), and 37.0 mole% Fe₂O₃ (907°C). The latter two eutectic points …