Microstructural Properties And Four-Point Bend Fatigue Behavior Of Ti-6.5al-2zr-1mo-1v Welded Joints By Electron Beam Welding, Peng Liu, Tongguang Zhai, Yuanbin Zhang

Chemical and Materials Engineering Faculty Publications

With the help of a four-point-bend of fatigue rig, high-cycle fatigue tests were carried out on an Ti–6.5Al–2Zr-1Mo-1V titanium alloy at room temperature, 20 Hz and R = 0.1 in ambient air. The test results indicated that the fatigue strength of base metal, 888 MPa, is about 120% of yield strength. The fatigue strength of joints is 814 MPa. It is about 110% of yield strength of base metal. When the loading stress is higher, the fatigue failure region is located in middle weld zone of weld face, which the cracks are propagated along coarse β phase’s grain boundary. When …