Sinteractive Anodic Powders Improve Densification And Electrochemical Properties Of Bazr0.8y0.2o3-O Electrolyte Films For Anode-Supported Solid Oxide Fuel Cells, Lei Bi, Emiliana Fabbri, Ziqi Sun, Enrico Traversa
Sinteractive Anodic Powders Improve Densification And Electrochemical Properties Of Bazr0.8y0.2o3-O Electrolyte Films For Anode-Supported Solid Oxide Fuel Cells, Lei Bi, Emiliana Fabbri, Ziqi Sun, Enrico Traversa
Australian Institute for Innovative Materials - Papers
The difficult sintering of BaZr0.8Y0.2O3-δ(BZY20) powders makes the fabrication of anode-supported BZY20 electrolyte films complex. Dense BZY20 membranes were successfully fabricated on anode substrates made of sinteractive NiO-BZY20 powders, prepared by a combustion method. With respect to traditional anode substrates made of powders prepared by mechanical mixing, the anode substrates made of the wet-chemically synthesized composite NiO–BZY20 powders significantly promoted the densification of BZY20 membranes: dense BZY20 films were obtained after co-pressing and co-firing at 1300°C, a much lower temperature than those usually needed for densifying BZY20 membranes. Improved electrochemical performance was …
Bazr(0.8)Y(0.2)O(3-Delta)-Nio Composite Anodic Powders For Proton-Conducting Sofcs Prepared By A Combustion Method, Lei Bi, Emiliana Fabbri, Ziqi Sun, Enrico Traversa
Bazr(0.8)Y(0.2)O(3-Delta)-Nio Composite Anodic Powders For Proton-Conducting Sofcs Prepared By A Combustion Method, Lei Bi, Emiliana Fabbri, Ziqi Sun, Enrico Traversa
Australian Institute for Innovative Materials - Papers
BaZr0.8Y0.2O3-∂ (BZY)-NiO composite powders with different BZY-NiO weight ratios were prepared by a combustion method as anodes for proton-conducting solid oxide fuel cells (SOFCs). After heating to 1100°C for 6 h, the composite powders were made of a well-dispersed mixture of two phases, BZY and NiO. Chemical stability tests showed that the BZY-NiO anodic powders had good stability against CO2, whereas comparative tests under the same conditions showed degradation for BaCe0.7Zr0.1Y0.2O3-∂- NiO, which is at present the most used anode material for proton-conducting …