Peridynamic Model For Dynamic Fracture In Unidirectional Fiber-Reinforced Composites, Wenke Hu, Youn Doh Ha, Florin Bobaru

Department of Mechanical and Materials Engineering: Faculty Publications

We propose a computational method for a homogenized peridynamics description of fiber-reinforced composites and we use it to simulate dynamic brittle fracture and damage in these materials. With this model we analyze the dynamic effects induced by different types of dynamic loading on the fracture and damage behavior of unidirectional fiber-reinforced composites. In contrast to the results expected from quasi-static loading, the simulations show that dynamic conditions can lead to co-existence of and transitions between fracture modes; matrix shattering can happen before a splitting crack propagates. We observe matrix–fiber splitting fracture, matrix cracking, and crack migration in the matrix, including …

Peridynamic Models For Dynamic Brittle Fracture, Wenke Hu

Department of Engineering Mechanics: Dissertations, Theses, and Student Research

Damage and failure in composite materials under dynamic loading has been extensively studied in experiments for several decades. Composite materials exhibit various damage and failure patterns under different loading rates, such as splitting and branching. Classical models cannot directly be applied to problems with discontinuous fields. A new nonlocal continuum model, peridynamics, has been proposed with the goal of solving dynamic fracture problems.

The J-integral has the physical significance of energy flow into the crack tip region. We present a rigorous derivation for the formulation of the J-integral in peridynamics using the crack infinitesimal virtual extension approach. We …