Proton Irradiation Effects On Semiconductor Cdse/Zns Core/Shell Nanocrystals, Stephen Graham Charter

Graduate Theses and Dissertations

The absorbance and photoluminescence measurement of semiconductor CdSe/ZnS core shell nanocrystals were reviewed and investigated after they were exposed to proton irradiation. The CdSe/ZnS core shell nanocrystals of 3.2nm and 4.4nm were commercially purchased and investigated. These nanocrystals were embedded in UV resin. Proton irradiation of energy 2MeV was applied at doses from 3 x 1013 protons cm-2 to 1.47 x 1015 protons cm-2 for both nanocrystal sizes. Absorbance measurements were conducted at 300K. Results from absorbance measurements showed slight broadening of the first exciton peak of both samples but was most noticeable in the 3.2nm nanocrystal sample. UV resin …