Long-Term Stability Of 14yt-4sc Alloy At High Temperature, Lulu Li, Weizong Xu, Mostafa Saber, Yuntian Zhu, Carl C. Koch, Ronald O. Scattergood
Long-Term Stability Of 14yt-4sc Alloy At High Temperature, Lulu Li, Weizong Xu, Mostafa Saber, Yuntian Zhu, Carl C. Koch, Ronald O. Scattergood
Mechanical and Materials Engineering Faculty Publications and Presentations
14YT alloy (Fe-14Cr-0.25wt.%Y2O3-0.4wt.%Ti) with 4 at.% Sc addition was previously reported to exhibit a nanoscale microstructure and high strength when annealed at temperatures up to 1000 °C (0.65Tm) for 1 hour. Here we report that the microstructure and mechanical behavior of 14YT-4Sc alloy after long-term annealing for up to 60 hours at 1000 °C. FIB analysis shows abnormal grain growth with annealing time, while a large fraction of the matrix still consists of nanoscale grains. TEM images reveal a slight growth of nano grains, with estimated grain growth exponent, n, to be 0.29. Sc-Ti-Y-O enriched nano oxide particles (nm) were …