Grain Oriented Crystallization, Piezoelectric, And Pyroelectric Properties Of (Baxsr₂ - X)Tisi₂O₈ Glass Ceramics, Jianping Zhang, Burtrand I. Lee, Robert W. Schwartz, Zhenya Ding
Grain Oriented Crystallization, Piezoelectric, And Pyroelectric Properties Of (Baxsr₂ - X)Tisi₂O₈ Glass Ceramics, Jianping Zhang, Burtrand I. Lee, Robert W. Schwartz, Zhenya Ding
Mechanical and Aerospace Engineering Faculty Research & Creative Works
Polar, nonferroelectric (BaxSr2 - x)TiSi2O8 glass ceramics with highly oriented crystallites were prepared by a gradient temperature heat treatment technique. The crystallization mechanism and microstructures of (BaxSr2 - x)TiSi2O8 glass ceramics were investigated by means of differential thermal analysis, x-ray diffraction and scanning electron microscopy, and the dielectric, piezoelectric and pyroelectric properties were investigated for various compositions. The results show that polar (BaxSr2 - x)TiSi2O8 glass ceramics have a low dielectric constant and a high hydrostatic figure of merit dh × gh = ~ 2500. This high hydrostatic figure of merit, along with other unique characteristics, such as no aging …
Measurement Of The Dielectric Strength Of Titanium Dioxide Ceramics, Wayne Huebner, J. M. Lundstrom, L. F. Rinehart, R. C. Pate, T. L. Smith, Mike L. Krogh
Measurement Of The Dielectric Strength Of Titanium Dioxide Ceramics, Wayne Huebner, J. M. Lundstrom, L. F. Rinehart, R. C. Pate, T. L. Smith, Mike L. Krogh
Materials Science and Engineering Faculty Research & Creative Works
Titanium dioxide ceramics (TiO2) are candidate materials for high energy density pulsed power devices. Experiments to quantify the dielectric strength of TiO2 have been performed on a limited number of unoptimized samples. A high voltage test set was constructed to test the titanium dioxide. All samples had a relative dielectric constant of 100, all samples were of 3 mm nominal thickness, and all tests were performed in water dielectric to reduce the effect of the triple point field enhancement at the electrode edge. Both single layer and laminated samples were tested and the breakdown field strengths were recorded. Voltage risetimes …