Articles 1 - 3 of 3
Full-Text Articles in Engineering
Evaluation Of Corrosion Properties Of Proprietary Metal Alloy Stents For In-Vivo Use, Michael David Bremner
Evaluation Of Corrosion Properties Of Proprietary Metal Alloy Stents For In-Vivo Use, Michael David Bremner
Materials Engineering
To assess corrosion rates of metal alloy bio-absorbable stents an experimental set-up was designed to mimic the coronary artery environment. The artery was modeled using 4mm diameter Tecoflex tubing and the metal alloy stents were inserted into the tubing using a catheter. As is the case in cardiac surgery, the catheter with the stent and a microballoon were maneuvered to the desired position. The microballoon was then slowly inflated to expand the stent and compress it against the tubing walls. The catheter and microballoon were then withdrawn. A circulating pump system was set up to cycle fetal bovine serum (FBS) …
Evaluation Of Forging Strain For Maximum Grain Size In Open-Die Forged 6061 Aluminum, Eric Strehl
Evaluation Of Forging Strain For Maximum Grain Size In Open-Die Forged 6061 Aluminum, Eric Strehl
Materials Engineering
In an effort to maximize grain growth of open-die forged 6061 aluminum alloy parts, samples from three of Weber Metals’s suppliers (Hidal Co-Almex USA Inc., TST Inc., and Vista Metals Corp.; to be called Supplier H, Supplier T, Supplier V respectively) were cut into cylinders with diameters of 0.75˝ and heights of 2˝, and put through a simulated forging process and heat treatment. It is possible that additional alloying elements may be promoting or inhibiting grain growth in the final part. Maximizing grain growth for aluminum alloy parts results in improved resistance to intergranular corrosion. Samples from each vendor had …
Comparison Of Polyurethane And Polysiloxane Coating Systems In Marine Environments, Jake Jarman, Jessica Salvatin
Comparison Of Polyurethane And Polysiloxane Coating Systems In Marine Environments, Jake Jarman, Jessica Salvatin
Materials Engineering
This project investigates the performance benefits of polysiloxane and polyurethane coating systems for corrosion protection in marine environments. PPG Industries Amercoat 450H and International Paint Interthane 990HS were the polyurethane topcoats tested. PPG Industries Ameron PSX 700 (New Blend) and International Paint Interfine 878 were the polysiloxane topcoats tested. Each coating was sprayed onto carbon steel panels that were prepared through hand blasting with glass beads. Scribed and unscribed panels were tested in a salt fog chamber for 1,200 hours according to ASTM Standard B0117-11 and in a UV/Humidifier for 1,650 hours according to ASTM Standard D4587-11. Panels were tested …