A New Spectroscopic Method For The Non-Destructive Characterization Of Weathering Damage In Plastics, Andrew Robert George
A New Spectroscopic Method For The Non-Destructive Characterization Of Weathering Damage In Plastics, Andrew Robert George
Theses and Dissertations
The weathering of plastics and composites is a problem because of the loss of both physical and mechanical properties that it causes in these materials. But this weathering effect has been difficult, and in some cases, impossible to characterize without the destruction of the plastic or composite part. Clearly a rapid, reliable, and non-destructive test for the extent of the weathering damage is critically needed. A recent problem that arose at Superyacht Solutions, a boat repair company in Australia, required a solution to just this problem. Such a test was developed for Superyacht Solutions, and is being applied across a …
An Analysis Of Microstructure And Corrosion Resistance In Underwater Friction Stir Welded 304l Stainless Steel, Tad Dee Clark
An Analysis Of Microstructure And Corrosion Resistance In Underwater Friction Stir Welded 304l Stainless Steel, Tad Dee Clark
Theses and Dissertations
An effective procedure and parameter window was developed for underwater friction stir welding (UWFSW) 304L stainless steel with a PCBN tool. UWFSW produced statistically significant: increases in yield strengths, decreases in percent elongation. The ultimate tensile strength was found to be significantly higher at certain parameters. Although sigma was identified in the UWFSWs, a significant reduction of sigma was found in UWFSWs compared to ambient FSWs. The degree of sensitization in UWFSWs was evaluated using double loop EPR testing and oxalic acid electro-etched metallography. Results were compared to base metal, ambient FSW, and arc welds. Upper and lower sensitization localization …