Carbon Fiber Recycling: Delamination System, Aaron Eastman
Carbon Fiber Recycling: Delamination System, Aaron Eastman
All Undergraduate Projects
The production of composite wings at Boeing causes carbon fiber waste and CWU Mechanical Engineering Technology students have been tasked in designing a carbon fiber recycling system. This project was brought forth and funded by the Joint Center for Aerospace Technology Innovation (JCATI). There are three subsystems that make up the carbon fiber recycling system, the delamination system, shredding system, and the oven. The purpose of this project was to increase the efficiency and effectiveness of the delamination system of the carbon fiber recycling system. The old system reached approximately 30-40 percent delamination with one pass through the system, and …
Carbon Oxidation At The Atomic Level: A Computational Study On Oxidative Graphene Etching And Pitting Of Graphitic Carbon Surfaces, Simon Schmitt
Carbon Oxidation At The Atomic Level: A Computational Study On Oxidative Graphene Etching And Pitting Of Graphitic Carbon Surfaces, Simon Schmitt
Theses and Dissertations--Mechanical Engineering
In order to understand the oxidation of solid carbon materials by oxygen-containing gases, carbon oxidation has to be studied on the atomic level where the surface reactions occur. Graphene and graphite are etched by oxygen to form characteristic pits that are scattered across the material surface, and pitting in turn leads to microstructural changes that determine the macroscopic oxidation behavior. While this is a well-documented phenomenon, it is heretofore poorly understood due to the notorious difficulty of experiments and a lack of comprehensive computational studies. The main objective of the present work is the development of a computational framework from …
Effects Of Corrugations On Stiffness Properties Of Composite Beams For Structural Applications, Jane Xiao
Effects Of Corrugations On Stiffness Properties Of Composite Beams For Structural Applications, Jane Xiao
Master's Theses
Composites have high strength-to-weight ratios, which is particularly desired for applications with weight restrictions. Common composite materials such as carbon fiber reinforced plastic (CF) and fiber glass reinforced plastic (FG) were used in this research. While composite materials possess high stiffness and strength properties, the stiffness of composite laminates may be maximized by changing the geometry. By adding corrugations, the flexural stiffness is increased in one direction compared to the stiffness of a flat part with the same amount of material. Thus, stiffness increases without a change in weight. The primary goal of this research was to investigate the stiffness …
Mode I Fracture Toughness Of Eight-Harness-Satin Carbon Cloth Weaves For Co-Cured And Post-Bonded Laminates, Josh E. Smith
Mode I Fracture Toughness Of Eight-Harness-Satin Carbon Cloth Weaves For Co-Cured And Post-Bonded Laminates, Josh E. Smith
Master's Theses
Mode I interlaminar fracture of 3k 8-Harness-Satin Carbon cloth, with identical fill and weft yarns, pre-impregnated with Newport 307 resin was investigated through the DCB test (ASTM D5528). Crack propagations along both the fill and weft yarns were considered for both post-bonded (co-bonded) and co-cured laminates. A patent-pending delamination insertion method was compared to the standard Teflon film option to assess its applicability to mode I fracture testing. The Modified Beam Theory, Compliance Calibration method, and Modified Compliance Calibration method were used for comparative purposes for these investigations and to evaluate the validity of the proposed Equivalent Stiffness (EQS) method. …