Engineering Commons^™

Solution Casting And Mechanical Testing Of Arabinan-Cellulose Nanocomposites, Kevin Su, Alina Lusebrink

Materials Engineering

The purpose of this work was to investigate methods to produce consistent, reliable, and testable thin films of arabinan-cellulose nanocomposites. Mechanical properties and composition of the Opuntia ficus-indica cactus spines served as motivation for this research. The high specific strength and stiffness, biodegradability, and sustainability of these spines inspired the creation of composites fabricated from the same materials found in cactus spines: arabinan and nanocrystalline cellulose (NCC). Arabinan serves as the matrix material and NCC as the reinforcement. To explore the feasibility of using a non-toxic solvent, different solution casting techniques with water as a solvent were investigated. Ultrasonication was …

Biaxial & Twist Testing Of Composite Carbon-Fiber Sandwich Panels For Automotive Racing Vehicles, Erik Eckberg

Materials Engineering

Composite sandwich panels were constructed with 4-ply plain weave carbon-fiber/epoxy face sheets in the 0^o/45^o/0^o/45^o orientation and 1/8^th inch Nomex honeycomb core. The panels were cut into 5-inch square test plates for mechanical testing. All testing was done on a fixture designed and fabricated by Pratt & Miller Engineering and installed on an Instron testing system at Cal Poly. The twist test was performed by supporting diagonal corners of the plate while simultaneously loading the opposite two corners at a crosshead rate of .06 in/min (ASTM 3044-94R11). Out of 10 panels tested, …

Investigating The Mechanical Properties Of Compression Molded Carbon Fiber Reinforced Sheet Molding Compound, Bradley A. Jones

Materials Engineering

Callaway Golf receives a proprietary blend of prepreg material from Quantum Composites. Callaway processes the prepreg in-house and supplied 254mm x 254mm x 1.3mm panels of carbon fiber sheet molding compound (CFSMC) for characterizing. Tensile strength was analyzed by conducting tensile tests per ASTM D3039. Tensile coupons were cut to 254mm long by 25.4mm wide. Tabs were constructed from 1.6mm thick GFRP printed circuit board material. A commercial grade two part epoxy was used to bond the tabs to the CFSMC. Tensile results were inconclusive due to consistent fractures occurring outside the gauge lengths of the specimens.

Flexure strength was …