Pitting Corrosion Of 410 Stainless Steel In Hcl Solutions, Paul D. Krell

Williams Honors College, Honors Research Projects

410 stainless steel (SS) is a material used in HCl services, such as distillation column trays in oil refineries. Unlike other alloys, however, the oil refining industry lacks a good reference for the corrosion rate of 410 SS at the varying HCl concentrations and temperatures the material might experience as trays in crude unit distillation columns. The goal of this project is to fill that knowledge gap. The corrosion behavior of 410 SS in HCl environments of pH 0.50, 1.25, 2.25, 3.25, and 4.25 at temperatures of 38, 52, 79, and 93°C was investigated using several methods. Cyclic potentiodynamic polarization …

Rubber Additives To Concrete Specimens, Kendall J. Sweitzer, Mary Mccannon

Williams Honors College, Honors Research Projects

Rubber, as an additive to concrete, would hypothetically cause a concrete specimen to take on some mechanical characteristics of the rubber to a certain degree. In particular, the concrete’s durability should increase when exposed to fluctuating temperature conditions due to the rubber additive. This experiment sets out to test crumb rubber as a concrete additive, cured under various atmospheric conditions. The effects shall be measured via a simple concrete compression test.

Unfortunately, several errors took place during experimental process that led to inconclusive results. However, it can be reasonably considered from testing Matrix One that the addition of crumb rubber …