Characterization Of Impact Damage And Fiber Reinforced Polymer Repair Systems For Metallic Utility Poles, Cara Johnson
Characterization Of Impact Damage And Fiber Reinforced Polymer Repair Systems For Metallic Utility Poles, Cara Johnson
Electronic Theses and Dissertations
Previous studies have demonstrated that the behavior of fiber reinforced polymers (FRPs) bonded to metallic utility poles are governed by the following failure modes; yielding of the metallic substrate, FRP tensile rupture, FRP compressive buckling, and debonding of FRP from the substrate. Therefore, an in situ method can be devised for the repair of utility poles, light poles, and mast arms that returns the poles to their original service strength. This thesis investigates the effect of damage due to vehicular impact on metallic poles, and the effectiveness of externally-bonded FRP repair systems in restoring their capacity. Damage is simulated experimentally …
Failure Analysis Of Impact-Damaged Metallic Poles Repaired With Fiber Reinforced Polymer Composites, Robert Arthur Slade
Failure Analysis Of Impact-Damaged Metallic Poles Repaired With Fiber Reinforced Polymer Composites, Robert Arthur Slade
Electronic Theses and Dissertations
Metallic utility poles, light poles, and mast arms are intermittently damaged by vehicle collision. In many cases the vehicular impact does not cause immediate failure of the structure, but induces localized damage that may result in failure under extreme service loadings or can promote degradation and corrosion within the damaged region. Replacement of these poles is costly and often involves prolonged lane closures, service interruption, and temporary loss of functionality. Therefore, an in situ repair of these structures is required. This thesis examines the failure modes of damaged metallic poles reinforced with externally-bonded fiber reinforced polymer (FRP) composites. Several FRP …