Rock Bolt Corrosion - An Experimental Study, Naj Aziz, P Craig, Jan Nemcik, Faisal Hai
Rock Bolt Corrosion - An Experimental Study, Naj Aziz, P Craig, Jan Nemcik, Faisal Hai
Faisal I Hai
The effect of long term exposure of full size bolts to corrosive environments is presented. A special test rig was used to test four bolts under different loading conditions. Four X-grade identical profile bolts, each 21·7 mm core diameter (23·7 mm full diameter) were subjected to prolonged corrosion testing using acid sulphate water. The pH value of the circulated water varied between 3·4 and 4·3. The corrosion exposure test period lasted 3·5 years. Two bolts were axially loaded to 10 t and 20 t force respectively, the third bolt was subjected to a 360 Nm torsion load and the fourth …
Thermodynamic Considerations Of The Corrosion Of Nickel Ferrite Refractory By Na3alf6-Alf3-Caf2-Al 2o3 Bath, Raymond Longbottom, Sharon Nightingale, Brian Monaghan
Thermodynamic Considerations Of The Corrosion Of Nickel Ferrite Refractory By Na3alf6-Alf3-Caf2-Al 2o3 Bath, Raymond Longbottom, Sharon Nightingale, Brian Monaghan
Brian Monaghan
Thermodynamic analysis was carried out to interpret the results of corrosion testing of nickel ferrite samples in cryolite-based baths. The equilibrium between cryolite-based baths and nickel ferrite was considered. Isopleths between cryolite-based baths and nickel ferrite confirmed that for the temperature range of interest (1223-1273 K) there was limited solubility of nickel ferrite in the bath. To better understand the formation of the metal from nickel ferrite, the effect of reducing potentials on nickel ferrite and nickel ferrite-cryolite-based bath systems were considered. The formation of a metal phase was predicted at relatively high pO2. The metal phase was nickel-rich at …