Engineering Commons^™

The Influence Of Organic Pigments On Coating Properties, Sarah Medeiros

Williams Honors College, Honors Research Projects

Abstract

The purpose of this project was to identify the qualities of two synthesized organic pigments added to a coating. These high-performance pigments were benzodipyrrolidone and benzodifuranone, which are π-conjugated monomers. These pigments were each formulated into two different pigment concentrations and compared with a control that had no pigment. This project is limited by time constraints and the number of variables that can be tested in that time. Performance testing was conducted to evaluate the qualities of these coatings. The results demonstrated that the coatings were reproducible and most tests had results that were equal to or exceeded the …

Magnesium-Titanium Alloys For Biomedical Applications, Ilona Hoffmann

Theses and Dissertations--Chemical and Materials Engineering

Magnesium has been identified as a promising biodegradable implant material because it does not cause systemic toxicity and can reduce stress shielding. However, it corrodes too quickly in the body. Titanium, which is already used ubiquitously for implants, was chosen as the alloying element because of its proven biocompatibility and corrosion resistance in physiological environments. Thus, alloying magnesium with titanium is expected to improve the corrosion resistance of magnesium.

Mg-Ti alloys with a titanium content ranging from 5 to 35 at.-% were successfully synthesized by mechanical alloying. Spark plasma sintering was identified as a processing route to consolidate the alloy …

Evaluation Of Corrosion Properties Of Proprietary Metal Alloy Stents For In-Vivo Use, Michael David Bremner

Materials Engineering

To assess corrosion rates of metal alloy bio-absorbable stents an experimental set-up was designed to mimic the coronary artery environment. The artery was modeled using 4mm diameter Tecoflex tubing and the metal alloy stents were inserted into the tubing using a catheter. As is the case in cardiac surgery, the catheter with the stent and a microballoon were maneuvered to the desired position. The microballoon was then slowly inflated to expand the stent and compress it against the tubing walls. The catheter and microballoon were then withdrawn. A circulating pump system was set up to cycle fetal bovine serum (FBS) …

Comparison Of Polyurethane And Polysiloxane Coating Systems In Marine Environments, Jake Jarman, Jessica Salvatin

Materials Engineering

This project investigates the performance benefits of polysiloxane and polyurethane coating systems for corrosion protection in marine environments. PPG Industries Amercoat 450H and International Paint Interthane 990HS were the polyurethane topcoats tested. PPG Industries Ameron PSX 700 (New Blend) and International Paint Interfine 878 were the polysiloxane topcoats tested. Each coating was sprayed onto carbon steel panels that were prepared through hand blasting with glass beads. Scribed and unscribed panels were tested in a salt fog chamber for 1,200 hours according to ASTM Standard B0117-11 and in a UV/Humidifier for 1,650 hours according to ASTM Standard D4587-11. Panels were tested …