Flux Pinning Mechanism In Bafe1.9ni0.1as2 Single Crystals: Evidence For Fluctuation In Mean Free Path Induced Pinning, M Shahbazi-Manshadi, X L Wang, K Y Choi, S X. Dou
Flux Pinning Mechanism In Bafe1.9ni0.1as2 Single Crystals: Evidence For Fluctuation In Mean Free Path Induced Pinning, M Shahbazi-Manshadi, X L Wang, K Y Choi, S X. Dou
Shi Xue Dou
The flux pinning mechanism of BaFe1.9Ni0.1As2 superconducting crystals have been investigated systematically by magnetic measurements up to 13 T at various temperatures. The field dependence of the critical current density, Jc, was analysed within the collective pinning model. A remarkably good agreement between the experimental results and theoretical dl pinning curve is obtained, which indicates that pinning in BaFe1.9Ni0.1As2 crystal originates from spatial variation of the mean free path. Moreover, the normalized pinning force density, Fp, curves versus h1/4B/Birr (Birr is the irreversibility field) were scaled using the Dew-Hughes model. Analysis suggests that point pinning alone cannot explain the observed …
In-Field Jc Improvement By Oxygen-Free Pyrene Gas Diffusion Into Highly Dense Mgb2 Superconductor, Minoru Maeda, Jung Ho Kim, Y Zhao, Yoon-Uk Heo, K Takase, Y Kubota, C Moriyoshi, F Yoshida, Y Kuroiwa, S X. Dou
In-Field Jc Improvement By Oxygen-Free Pyrene Gas Diffusion Into Highly Dense Mgb2 Superconductor, Minoru Maeda, Jung Ho Kim, Y Zhao, Yoon-Uk Heo, K Takase, Y Kubota, C Moriyoshi, F Yoshida, Y Kuroiwa, S X. Dou
Shi Xue Dou
Oxygen-free pyrene gas as a carbon (C) dopant was delinked and incorporated into highly dense MgB2 structure via a gas phase diffusion method. The technique offers the advantages that molecular C is homogeneously distributed into MgB2 and substituted at the boron sites without any severe deterioration of grain connectivity. The C substitution causes a significant shrinkage of the a-lattice parameter and an increase in the lattice strain, resulting in high disorder. The introduction of structural disorder as a result of C doping leads to a considerable enhancement of the in-field critical current density (Jc) and upper critical field.
Synthesis And Optimization Of Fluorine-Free Y And Cu Precursor Solution For Mod Processing Of Ybco Coated Conductor, Jaimoo Yoo, Young-Kuk Kim, Kookchae Chung, Jaewoong Ko, Xiaolin Wang, S X. Dou
Synthesis And Optimization Of Fluorine-Free Y And Cu Precursor Solution For Mod Processing Of Ybco Coated Conductor, Jaimoo Yoo, Young-Kuk Kim, Kookchae Chung, Jaewoong Ko, Xiaolin Wang, S X. Dou
Shi Xue Dou
MOD solutions for YBCO coated conductors were synthesized with fluorine-free Y & Cu precursor. The fluorine content in the precursor solution was significantly reduced and a fast calcination profile was realized. A crack-free & thick precursor film was successfully obtained just after less than 2 hours of calcination in wet O2 atmosphere. Optimization of the precursor solution with Sm addition enables further improvement of thickness and uniformity of precursor films. The calcinated precursor film was successfully converted to dense and uniform YBCO film after annealing in wet Ar/O2 atmosphere. The measured critical current value was about 273 A/cm-w (Jc ~ …
Flux-Pinning Mechanism In Silicone-Oil Doped Mgb2: Evidence For Charge-Carrier Mean Free Path Fluctuation Pinning, Shaban R. Ghorbani, Xiaolin Wang, S X. Dou, Sung-Ik Lee, Md S. Hossain
Flux-Pinning Mechanism In Silicone-Oil Doped Mgb2: Evidence For Charge-Carrier Mean Free Path Fluctuation Pinning, Shaban R. Ghorbani, Xiaolin Wang, S X. Dou, Sung-Ik Lee, Md S. Hossain
Shi Xue Dou
Flux-pinning mechanism of MgB2 doped with 10 wt % silicone-oil sintered at low and high temperatures has been investigated by magnetic measurements. The field dependence of the critical current density, jc(B), was analysed within the collective pinning model. A crossover field, Bsb, from the single vortex to the small vortex bundle-pinning regime was observed. For both types of sintered samples, the temperature dependence of Bsb(T) at low temperature is in good agreement with the δl pinning mechanism, i.e., pinning associated with charge-carrier mean free path fluctuation. At temperatures close to the critical temperature, however, there is evidence for δTc pinning, …