Assessment Of Cu(In, Ga)Se₂ Solar Cells Degradation Due To Water Ingress Effect On The Cds Buffer Layer, Deewakar Poudel, Benjamin Belfore, Shankar Karki, Grace Rajan, Sina Soltanmohammad, Angus Rockett, Sylvain Marsillac
Assessment Of Cu(In, Ga)Se₂ Solar Cells Degradation Due To Water Ingress Effect On The Cds Buffer Layer, Deewakar Poudel, Benjamin Belfore, Shankar Karki, Grace Rajan, Sina Soltanmohammad, Angus Rockett, Sylvain Marsillac
Electrical & Computer Engineering Faculty Publications
The effect of water ingress on the surface of the buffer layer of a Cu(In, Ga)Se2 (CIGS) solar cell was studied. Such degradation can occur either during the fabrication process, if it involves a chemical bath as is often the case for CdS, or while the modules are in the field and encapsulants degrade. To simulate the impact of this moisture ingress, devices with a structure sodalime glass/Mo/CIGS/CdS were immersed in deionized water. The thin films were then analyzed both pre and post water soaking. Dynamic secondary ion mass spectroscopy (SIMS) was performed on completed devices to analyze impurity diffusion …
Characterization Of Iron Oxides And Atmospheric Corrosion Of Steel, Sei Jin Oh
Characterization Of Iron Oxides And Atmospheric Corrosion Of Steel, Sei Jin Oh
Physics Theses & Dissertations
The study of corrosion behavior was performed using three different analytical techniques, which provided information on the formation, development and layering of iron oxides on the corrosion products as a function of atmospheric conditions, exposure time and type of steel. In particular, the protective layer formed on weathering steel was investigated as a function of different amounts of alloying elements in the steel, atmospheric conditions and exposure times. Combined together, the results provided a better understanding of the atmospheric corrosion behavior of steel, and formed a part of database of the atmospheric corrosion characteristics.
Accurate characterization of the iron oxides …