A Comparative Study Of Magnetic Behaviors In Tbni2, Tbmn2 And Tbni2mn, Jianli Wang, M F. Md Din, Shane Kennedy, F Hong, Stewart J. Campbell, A J. Studer, G H. Wu, Zhenxiang Cheng, S X. Dou
A Comparative Study Of Magnetic Behaviors In Tbni2, Tbmn2 And Tbni2mn, Jianli Wang, M F. Md Din, Shane Kennedy, F Hong, Stewart J. Campbell, A J. Studer, G H. Wu, Zhenxiang Cheng, S X. Dou
Shi Xue Dou
All TbNi2, TbMn2, and TbNi2Mn compounds exhibit the cubic Laves phase with AB2-type structure in spite of the fact that the ratio of the Tb to transition-metal components in TbNi2Mn is 1:3. Rietveld refinement indicates that in TbNi2Mn the Mn atoms are distributed on both the A (8a) and B (16d) sites. The values of the lattice constants were measured to be a = 14.348 Å (space group F-43 m), 7.618 Å, and 7.158 Å (space group Fd-3 m) for TbNi2, TbMn2, and TbNi2Mn, respectively. The magnetic transition temperatures TC were found to be TC = 38 K and TC …
Microstructures Of Conducting Polymers: Patterning And Actuation Study, Babita Gaihre, Bo Weng, Syed A. Ashraf, Geoffrey M. Spinks, Peter C. Innis, Gordon G. Wallace
Microstructures Of Conducting Polymers: Patterning And Actuation Study, Babita Gaihre, Bo Weng, Syed A. Ashraf, Geoffrey M. Spinks, Peter C. Innis, Gordon G. Wallace
Gordon Wallace
The conducting polymers exhibit electrochemically driven expansion and shrinkage due to ingress and egress of dopant ions in response to potential applied. In this paper, we report on patterning of microdots and microsquares of polypyrrole (PPy), poly(3,4-ethylenedioxythiophene) (PEDOT) and poly(3,3-dihexyl-3-4-dihydro-2H-thieno[3,4b][1,4]-dioxepine PProDOT(Hx) 2 and their behaviour under voltage change. Stainless steel mesh was used to deposit microdots and inkjet-printed cellulose girds were used to deposit microsqures of the conducting polymers on the ITO surface. It was found that PPy showed distinct actuation in the z direction while colour change was prominent in the case of PEDOT and PProDOT(Hx)2.
Aging Effect Evolution During Ferroelectric-Ferroelectric Phase Transition: A Mechanism Study, Zuyong Feng, Zhenxiang Cheng, Dongqi Shi, S X. Dou
Aging Effect Evolution During Ferroelectric-Ferroelectric Phase Transition: A Mechanism Study, Zuyong Feng, Zhenxiang Cheng, Dongqi Shi, S X. Dou
Shi Xue Dou
Aging can significantly modify the dielectric, piezoelectric, and ferroelectric performance of ferroelectrics. However, little attention has been paid to the aging effect during ferroelectric-ferroelectric phase transitions that is essentially correlated with real applications. In this letter, the authors report the aging effect evolution between two ferroelectric phases in an acceptor-doped piezoceramics. The results show that aging-induced double hysteresis loops were exhibited in different ferroelectric phases, but disappeared during ferroelectric-ferroelectric phase transitions, suggesting the mechanism that the intrinsic restoring force for the reversible switching of domains caused by the alignment of defect dipoles was weakened due to ferroelectric dipole reorientation.
Neutron Diffraction Study Of Mnniga2 - Structural And Magnetic Behaviour, Jianli Wang, L Ma, M Hofmann, M Avdeev, S J. Kennedy, S J. Campbell, M F. Md Din, M Hoelzel, G H. Wu, S X. Dou
Neutron Diffraction Study Of Mnniga2 - Structural And Magnetic Behaviour, Jianli Wang, L Ma, M Hofmann, M Avdeev, S J. Kennedy, S J. Campbell, M F. Md Din, M Hoelzel, G H. Wu, S X. Dou
Shi Xue Dou
MnNiGa2 crystallizes in the L21 (Heusler) structure and has a ferromagnetic ordering temperature TC ∼ 192 K. Rietveld refinement of the neutron diffraction patterns indicates that the Ga atoms occupy the equivalent 8c position, while Mn and Ni share the 4a (0, 0, 0) and 4b (0.5, 0.5, 0.5) sites with a mixed occupancy of Mn and Ni atoms. It is found that that ∼83% of Mn and ∼17% Ni are located at the 4a site while ∼83% of Ni and ∼17% Mn occupy the 4b site. There is no evidence of a magneto-volume effect around TC. In agreement with …