Corrosion Of Oil Pipeline: A Case Study On The Niger Delta Region Of Nigeria., Victor U. Okoro

Corrosion Research

Corrosion of oil pipelines in Nigeria, particularly in the Niger Delta region, has extensive and detrimental environmental and societal impacts. This issue results in substantial financial losses and reputational damage for oil companies operating in the area. Local communities suffer economically, affecting agriculture and food security. Furthermore, corrosion-related oil spills lead to air quality degradation by releasing volatile organic compounds and greenhouse gases, contributing to respiratory issues and worsening climate change.

These oil spill cleanups are costly and time-consuming, with estimated expenses reaching billions of dollars. Using the Nembe Creek Trunk Line (NCTL) case study, it is evident that addressing …

Corrosion Case Study On Pipeline, Kangze Ren

Corrosion Research

The Kashagan pipeline leaks were likely caused by sulfur stress corrosion cracking, a combined corrosion mechanism developed by the presence of high pressure, the high level of hydrogen sulfide(the main "ingredient" of sour gas), and poor metallurgical choice. Improper welding and poor metallurgical examination were blamed for causing the leaking issue. The purpose of the current review is to raise the alarm about the inappropriate corrosion management of Kashagan oil production and its societal and environmental consequences.

Novel And Fast Peridynamic Models For Material Degradation And Failure, Siavash Jafarzadeh

Department of Mechanical and Materials Engineering: Dissertations, Theses, and Student Research

Fracture is one of the main mechanisms of structural failure. Corroded surfaces with chemically-induced damage are, notably, potential sites for crack initiation and propagation in metals, which can lead to catastrophic failure of structures. Despite some progress in simulating fracture and damage using classical models, realistic prediction of complex damage progression and failure has been out of reach for many decades. Peridynamics (PD), a nonlocal theory introduced in 2000, opened up new avenues in modeling material degradation and failure. Existing numerical methods used to discretize PD equations, however, are quite expensive as the PD nonlocal interactions make them unaffordable for …

Self-Healing Microcapsules As Concrete Aggregates For Corrosion Inhibition In Reinforced Concrete, Homero Castaneda, Marwa Hassan, Miladin Radovic, Jose Milla

Publications

Reinforced Concrete (RC) structures are vital to the US’s civil infrastructure for their strength and versatility. Unfortunately, RC elements deteriorate rapidly when exposed to corrosive environments. One possible solution is to extend the life of RC elements and systems using microencapsulated corrosion inhibitors to reduce the rebar corrosion rate. The capsules house an anodic corrosion inhibitor agent including calcium nitrate (CN) and triethanolamine (TEA). The integration of such microencapsulated materials will enhance the durability and extend the useful life by controlling the corrosion precursors and the corrosion process during damage evolution. Therefore, this work aims to develop and characterize the …

Evaluation Of Organic Protective Coatings As Corrosion Prevention For The Interior Of Subsea Pipelines In Sour Gas Service, Faris M. Alkordy

FIU Electronic Theses and Dissertations

The purpose of this study was to examine the performance of several generic types of organic protective coatings as a corrosion protection method for the interior of subsea pipelines in sour gas media. The sour gas environment was simulated in the laboratory by the use of an Autoclave and the performance of the organic coatings was studied via the use of Electrochemical Impedance Spectroscopy (EIS) and Linear Polarization Resistance (LPR) tests to determine the coatings resistance, capacitance and corrosion behavior before and after the exposure to sour gas environment. The coating degradation and the corrosion products formed were examined by …

In-Vivo Corrosion And Fretting Of Modular Ti-6al-4v/Co-Cr-Mo Hip Prostheses: The Influence Of Microstructure And Design Parameters, Jose Luis Gonzalez Jr

FIU Electronic Theses and Dissertations

The purpose of this study was to evaluate the incidence of corrosion and fretting in 48 retrieved titanium-6aluminum-4vanadium and/or cobalt-chromium-molybdenum modular total hip prosthesis with respect to alloy material microstructure and design parameters. The results revealed vastly different performance results for the wide array of microstructures examined. Severe corrosion/fretting was seen in 100% of as-cast, 24% of low carbon wrought, 9% of high carbon wrought and 5% of solution heat treated cobalt-chrome. Severe corrosion/fretting was observed in 60% of Ti-6Al-4V components. Design features which allow for fluid entry and stagnation, amplification of contact pressure and/or increased micromotion were also shown …