Articles 1 - 2 of 2
Full-Text Articles in Engineering
Measuring The Mechanical Properties Of A Newly Developed Discontinuous Carbon Fiber And Epoxy Composite, Morgan Adams
Measuring The Mechanical Properties Of A Newly Developed Discontinuous Carbon Fiber And Epoxy Composite, Morgan Adams
Materials Engineering
Engineering firm Pratt & Miller have developed a new and previously untested carbon fiber/epoxy composite using a spray lay-up process similar to a process commonly used in fiberglass production. This new composite is made by using a pneumatic chop gun that simultaneously cuts the carbon fibers to a specific length and deposits the chopped fibers and resin onto surface of an exposed mold surface. The composite is then rolled down to flatten and better wet the fibers and then the whole mold is vacuum bagged at room temperature to cure. The flexural stiffness and flexural strength of the composite with …
Biaxial & Twist Testing Of Composite Carbon-Fiber Sandwich Panels For Automotive Racing Vehicles, Erik Eckberg
Biaxial & Twist Testing Of Composite Carbon-Fiber Sandwich Panels For Automotive Racing Vehicles, Erik Eckberg
Materials Engineering
Composite sandwich panels were constructed with 4-ply plain weave carbon-fiber/epoxy face sheets in the 0o/45o/0o/45o orientation and 1/8th inch Nomex honeycomb core. The panels were cut into 5-inch square test plates for mechanical testing. All testing was done on a fixture designed and fabricated by Pratt & Miller Engineering and installed on an Instron testing system at Cal Poly. The twist test was performed by supporting diagonal corners of the plate while simultaneously loading the opposite two corners at a crosshead rate of .06 in/min (ASTM 3044-94R11). Out of 10 panels tested, …