Application Of Voltammetry To Copper Electrodeposition, Louis Francis Toth Jr.

Doctoral Dissertations

"A study was undertaken to determine the feasibility of using voltammetry and scanning electron microscopy techniques to characterize copper deposition from an acid-sulfate electrolyte. The main process variables investigated were temperature and addition agents (chloride ion, glue, separan or thiourea) at different concentrations, over a range of current densities. Cathodes employed were either polycrystalline titanium or copper. Some long-time copper deposits were also made using Ti cathodes and the orientations of these deposits were determined by x-ray diffraction.

Observations of copper crystals produced during voltammetry scans, on a Ti cathode, indicated that a characteristic morphology was associated with each type …

Variables Affecting The Rate Of Solution Of Mold Inoculants In Cast Iron, Jose Osorno Fonnegra

Masters Theses

"The purpose of this investigation was to measure the effectiveness of an inoculant alloy reacting with molten cast iron in a reaction chamber properly located in the gating system.

The chemical composition of the gray iron was held constant while several metallurgical factors were varied to produce test samples with different cementite thicknesses. These chill depths were measured as an indication of the inoculation effectiveness.

Appreciable differences in chilling tendency were observed within the different variables studied. The results indicate that pouring temperature, as well as the other variables studied, are of considerable importance when dealing with inoculation of gray …

Corrosion And Electrochemical Behavior Of Indium And Indium-Bismuth Alloys In Hydrochloric Acid, Yar Ming Wang

Doctoral Dissertations

"The corrosion of In-Bi alloys was studied using X-ray, scanning electron microscopy, atomic absorption spectroscopy, and cyclic voltammetry techniques.

Calculated activation energy values indicated that the corrosion of In-Bi alloys was activation controlled. The effect of amine mixtures on the corrosion of In and In₂Bi (ß₁ phase) was studied. Morphological studies revealed that the porosity of the resulting physical surface structure was influential in determining the corrosion rate. In deaerated 3N HCl solutions, the selective dissolution of indium was the predominant mechanism in the corrosion of In-Bi alloys. The corrosion was always accompanied by a phase change …