Development Of Castrip Dual Phase Steel, Brenton Allen Hrebec

Masters Theses

“Thermomechanical processing necessary to produce DP 980 steel using CASTRIP hot band was investigated. The resultant steel has an ultimate tensile strength of 1038 MPa, yield strength of 744 MPa, and total elongation of 8.6%. These mechanical properties were achieved by batch annealing the hot band at 649°C for 48 hours and cold rolling to a 20% reduction. The steel was continuously annealed to simulate a galvanization cycle with an intercritical temperature of 810°C. The possibility of improving the texture of the steel by warm rolling under dynamic strain aging conditions was investigated. Dynamic strain aging in the CASTRIP hot …

Development Of Stage-I Tempered High Strength Cast Steel For Ground Engaging Tools, Viraj Ashok Athavale

Doctoral Dissertations

"Ground Engaging Tools (GET) are the expendable replacement parts used in heavy machinery used with mining or construction equipment. GET’s protect the expensive machine components from the wear and tear found common in high-impact or high-abrasion environments. The goal of this project is to develop advanced next-generation alloy choices that outperforms the existing GET materials. A method of predicting tempered hardness of mixed microstructures was formulated. Using this model, two alloy series viz. Cr-Ni-Mo and Mn-Si-Mo-V were proposed and experimented with the goal of obtaining a high strength and impact resistant cast steel. Cast iterations of Cr-Ni-Mo alloy series were …

Oxide Inclusion Evolution And Factors That Influence Their Size And Morphology, Obinna M. Adaba

Doctoral Dissertations

"The evolution of oxide inclusion size distribution and the shape of the distribution during steelmaking and casting and the process variables that influence the inclusion characteristics at different stages were investigated and documented. A statistical method for transforming the 2D size distribution to their actual 3D distributions and the application of a kinetic model to determine nucleation and growth mechanisms were tested. Finally, laboratory experiments were performed to study the effects of preexisting inclusions, steel active oxygen content, and supersaturation on the size and morphology of Al₂O₃ inclusions.

The inclusion size, composition, and morphology following steel deoxidation …