Influence Of Nobler Metal Salt Additions Upon The Dissolution Rate Of Aluminum In Hydrofluoric Acid, Barry L. Basden

Masters Theses

"The rate of dissolution of aluminum in 2N HF upon the addition of nobler metallic salts was studied. Aluminum corrodes in HF due to the acid's ability to dissolve the protective oxide present on the surface. Rates were measured by the hydrogen evolution method. Salt additions of AgN0₃, CuSO₄, HAuC₄, and PtCl₄ to aluminum dissolving in 2N HF resulted in the electroless deposition of more or less coherent metals (from the salts mentioned) on the aluminum surface. The dissolution rate initially decreased in all of the cases and was attributed to the "blanketing effect" of the deposits. Ensuing increases of …

A Mechanical Metallurgical Method Of Predicting The Springback Tendencies Of A Bent Metal Strip, Jerrold Myles Alyea

Masters Theses

"Attempted substitution of new solid materials and composite metal strips for those materials presently being used in many applications now being pursued vigorously in industry. A serious problem was created because the newly proposed materials do not exhibit the same springback after bending as did the previously used materials in a particular bend angle and radius situation. Elementary bend theory and mechanical metallurgical techniques have been incorporated into a method which can be used to accurately predict the .2% offset yield strength of any proposed rolled-temper solid metal strip and some composite strips when they must exhibit the same springback …

Corrosion Rates And Electrokinetics Of Cobalt And Cobalt-Rich Cobalt-Iron Alloys In Sulfuric And Hydrochloric Acids, Cheng Tzong Horng

Masters Theses

"Corrosion rates for Co and Co-rich Co-Fe alloys were determined in sulfuric and hydrochloric acids under both deaerated and oxygenated conditions. For the purpose of comparison, corrosion rates of Co cut from metal sheet were also determined in the same environments as those of sintered alloys. Sintered alloys were inferior to solid Co as corrosion resistant materials. It was found that the surface was more corrosion resistant than the interior. Thus after long exposure to the corrosive acid, the samples became porous inside while the surfaces remained substantially intact. Oxygen had a pronounced effect in accelerating the corrosion of Co …

Pressure Welding Of Continuously Cast Nodular Iron, Gerald W. Wille

Masters Theses

"The objective of this study was to determine the feasibility of using pressure welding as a joining technique for swaged nodular iron.

Test pressure welds were produced with swaged continuous cast nodular iron at temperatures between 1750⁰F and 2050⁰F with welding pressures between 15,900 psi and 51,400 psi using an induction coil to heat the weld zone.

Pressure welds of greater strength than the as-received nodular iron were produced by swaging the material before welding. The optimum welding parameters were a temperature of 2050⁰F with a welding pressure of 46,700 psi.

On the basis of these tests it is concluded …

The Inert Gas Effect On The Rate Of Evaporation Of Zinc And Cadmium, Chu Sheng Wu

Masters Theses

"An experimental study has been made to investigate the effect of argon and helium on the rate of evaporation of zinc and cadmium under one atmosphere pressure at temperatures ranging from 500⁰C to 850⁰C. The experimental results were compared with the maximum rates calculated using the effusion formula as well as with values obtained using three different types of equations based on kinetic theory, diffusion theory, and empirical data. The rate of evaporation in this study appeared to be diffusion controlled. Equations have been derived for expressing the rate of evaporation of zinc and cadmium in both argon and helium …

Isotope Effect Of Interstitial Diffusion Of Carbon In A Dilute Fe-Si Alloy, Edward T. Yen

Masters Theses

"The isotope effect of carbon interstitial diffusion in a Fe-2.75at%Si alloy has been measured at -3.10°C using the disaccommodation technique. The disaccommodation has been analyzed in terms of two relaxation processes which are discussed on the basis of the reorientation mechanism of carbon interstitials at Fe-Fe sites and Fe-Si sites respectively. The ratios of the relaxation times [tau]₁₃/[tau]₁₂ are 1.0382 for the former and 1.0072 for the latter relaxation process. This result is discussed on the basis of many-body reaction rate theory"--Abstract, page ii.

The Effect Of Prior Cold Work On The Pressure Welding Of Ferritic Nodular Iron, Ronald Morris Ledbetter

Masters Theses

"The purpose of this investigation was to determine the effect of prior cold work by swaging on the pressure welding of ferritic nodular iron. Test pressure welds were produced from continuously cast ferritic nodular iron in the as cast condition and with prior cold work of 20, 30, 40, and 50 per cent reductions in area. Welding pressures of 23,500 psi, 35,300 psi, and 47,100 psi were employed. All welds were made at interface temperatures of 2000°F. Welds made with the as cast material at high welding pressures possessed relatively low tensile strengths due to the creation of planes of …

Lattice Parameters, Coefficients Of Thermal Expansion, Densities, And Lattice Perfection Of The Copper-Indium Primary Solid Solutions, Lin Sheng Yu

Masters Theses

"Precise measurements of lattice parameters and densities of the alpha-phase Cu-In solid solutions were made at temperatures of 25°C. The thermal expansion coefficients between 15 and 65°C, the solid solubility of In in Cu at 650°C, and the soundness of crystal structure resulting from alloying were determined. The Cu-In alloys were prepared from high purity (99.999%) Cu and In by melting both metals inside evacuated quartz tubes. The solidified alloys were annealed and then examined by X-ray for homogeneity...The slowly solidified alpha-phase alloys gave densities lower than the theoretical (X-ray) values due to the presence of shrinkage microporosity. This density …