Effects Of Prior Aging At 191°C On Creep Response Of Im7/Bmi 5250-4, Robert A. Salvia
Effects Of Prior Aging At 191°C On Creep Response Of Im7/Bmi 5250-4, Robert A. Salvia
Theses and Dissertations
The creep behavior of IM7/BMI 5250-4 with fiber orientations of [± 45] and [0/90] that were aged in air at 191 °C for up to 1000 hours was evaluated. The total weight loss during the aging process was also evaluated. Weight loss due to aging was 0.64% for the [0/90] fiber orientation and 0.72% for the [± 45] fiber orientation. Tensile tests to failure were conducted to establish tensile properties. The [0/90] specimens have a much higher stiffness and Ultimate Tensile Strength (UTS) values than the [± 45] specimens. The tensile tests of the aged specimens revealed that the Ultimate …
Tension-Compression Fatigue Behavior Of A Carbon Fiber/Epoxy (Im7/Epon 862) Composite Fabricated Using Vacuum Assisted Resin Transfer Molding Process, David W. Katwyk
Tension-Compression Fatigue Behavior Of A Carbon Fiber/Epoxy (Im7/Epon 862) Composite Fabricated Using Vacuum Assisted Resin Transfer Molding Process, David W. Katwyk
Theses and Dissertations
New composite materials and processing methods are continually being developed for use in high performance aerospace systems. One of these new processing methods is the vacuum assisted resin transfer molding (VARTM) process, which shows promise in producing large structural components that have good properties at a lower cost than traditional manufacturing methods. Future widespread use of components manufactured using the VARTM process depends on understanding how these components perform under service conditions, specifically under impact and fatigue conditions. The tension-compression fatigue behavior of a four-harness satin weave carbon fiber/epoxy (IM7/EPON 862) composite manufactured using the VARTM process is investigated in …