Effects Of Shot-Peening On High Cycle Fretting Fatigue Behavior Of Ti-6al-4v, Halil I. Yuksel

Theses and Dissertations

Effects of Shot-peening on High Cycle Fretting Fatigue behavior of Ti-6Al-4V were investigated. Experiments were performed with 6.35 mm thick specimens which provided S/N curves. After the tests, it was observed that the specimens failed near the trailing edge of contact. Scanning Electron Microscopy showed that cracks initiated on the contact surface for 6.35 mm, and at the depth of specimen ranging from 200 to 300 microns for 3.81 mm thick specimens. Initial crack orientation was around 37 and 42 degrees respectively for 6.35 and 3.81 mm thicknesses. Finite Element Analysis (FEA) was conducted, and using FEA results, Smith-Watson-Topper, Findley, …