Mode I Fracture Toughness Of Eight-Harness-Satin Carbon Cloth Weaves For Co-Cured And Post-Bonded Laminates, Josh E. Smith

Master's Theses

Mode I interlaminar fracture of 3k 8-Harness-Satin Carbon cloth, with identical fill and weft yarns, pre-impregnated with Newport 307 resin was investigated through the DCB test (ASTM D5528). Crack propagations along both the fill and weft yarns were considered for both post-bonded (co-bonded) and co-cured laminates. A patent-pending delamination insertion method was compared to the standard Teflon film option to assess its applicability to mode I fracture testing. The Modified Beam Theory, Compliance Calibration method, and Modified Compliance Calibration method were used for comparative purposes for these investigations and to evaluate the validity of the proposed Equivalent Stiffness (EQS) method. …

Synthesis Of Carbon Nanotubes Using High Voltage And High Frequency Induction Field, Kalty Vazquez

FIU Electronic Theses and Dissertations

The fields of nanomaterial and nanostructures are some of the fastest growing fields in material science today. Carbon nanotubes are at the forefront of these fields and their unique mechanical and electrical properties are of great interest to those working in multiple engineering fields.

The overall objective of this study was to design and develop a new process and the equipment necessary, to synthesize carbon nanotubes using high voltage and a high-frequency induction field. This was the first time that a high voltage and an induction field have been used simultaneously in high yield production of carbon nanotubes.

The source …