Carbonation Service Life Prediction Of Existing Concrete Viaduct/Bridge Using Time-Dependent Reliability Analysis, Ming-Te Liang, Ran Huang, Shen-Ann Fang
Carbonation Service Life Prediction Of Existing Concrete Viaduct/Bridge Using Time-Dependent Reliability Analysis, Ming-Te Liang, Ran Huang, Shen-Ann Fang
Journal of Marine Science and Technology
This paper examines the predicted carbonation life of an existing concrete viaduct/bridge in the atmospheric environment based on probability and reliability indices. The probability is dependent upon the carbonation rate, carbonation remainder, concrete quality, and concrete cover. The carbonation life is defined as the service life of reinforced concrete (RC) or prestressed concrete (PC) structure at the beginning of time of steel corrosion when concrete cover surfers from carbonation and loses the protection function to steel. The carbonation life is equivalent to the initiation time of corrosion of reinforcement. Both the Chorng-ching viaduct and Wannfwu bridge were offered as illustrative …
Rust-Expansion-Crack Service Life Prediction Of Existing Reinforced Concrete Bridge/Viaduct Using Time-Dependent Reliability Analysis, Ming-Te Liang, Jiang-Jhy Chang, Han-Tung Chang, Chi-Jang Yeh
Rust-Expansion-Crack Service Life Prediction Of Existing Reinforced Concrete Bridge/Viaduct Using Time-Dependent Reliability Analysis, Ming-Te Liang, Jiang-Jhy Chang, Han-Tung Chang, Chi-Jang Yeh
Journal of Marine Science and Technology
It is necessary to develop a calculation method to help in the making of feasible, reliable, and serviceable predictions for the service lives of bridge or viaduct structures. This article presents the basis for doing rust-expansion-crack service life predictions for existing reinforced concrete (RC) bridges and viaducts in chloride-laden environments based on timedependant reliability modeling due to the corrosion of steel in concrete. The corrosion process has three stages, the initiation (diffusion or carbonation) time (ti = tc), the depassivation time (tp), and the propagation (corrosion) time (tcorr). The rustexpansion-crack service lives (tcr) of existing RC bridges or viaducts can …