Full-Text Articles in Engineering
A Comparative Study Of Strength And Stiffness Of Thin-Walled Specimens Fabricated By Fdm And 3d Printing Technologies, Miranda Rodrigo
A Comparative Study Of Strength And Stiffness Of Thin-Walled Specimens Fabricated By Fdm And 3d Printing Technologies, Miranda Rodrigo
Theses and Dissertations
Rapid Prototyped part failure constitutes a major issue for both RP providers and customers. When parts fail the reputation of the vendor is heavily deteriorated, customer dissatisfaction increase and replacement of the broken parts is often necessary to avoid the loss of future business. Product design teams often run into situations where Rapid Prototyped parts are not able to withstand shipping and handling and delivered broken or while demonstrating and examining the parts. When done in the face of customers this builds a perception of poor quality and lack of aptitude on the design group as well as the RP …
Mechanical Properties And Mems Applications Of Carbon-Infiltrated Carbon Nanotube Forests, Walter C. Fazio
Mechanical Properties And Mems Applications Of Carbon-Infiltrated Carbon Nanotube Forests, Walter C. Fazio
Theses and Dissertations
This work explores the use of carbon-infiltrated carbon nanotube (CI-CNT) forests as a material for fabricating compliant MEMS devices. The impacts of iron catalyst layer thickness and carbon infiltration time are examined. An iron layer of 7nm or 10nm with an infiltration time of 30 minutes produces CI-CNT best suited for compliant applications. Average maximum strains of 2% and 2.48% were observed for these parameters. The corresponding elastic moduli were 5.4 GPa and 4.1 GPa, respectively. A direct comparison of similar geometry suggested CI-CNT is 80% more flexible than single-crystal silicon. A torsional testing procedure provided an initial shear modulus …