Engineering Commons^™

Preparation And Characterization Of The Silane-Phosphonic Acid Composite Passivation Coating For Electrogalvanized Steel, Yong Guan, Jian-Guo Liu, Chuan-Wei Yan

Journal of Electrochemistry

A new silane-phosphonic acid composite passivation coating process has been developed for the protection of electrogalvanized steel based on N-(β-aminoethyl)-γ-aminopropyltrimethoxysilane(AAPTMS),γ-(2,3-epoxypropoxy)propyltrimethoxy-silane(GPTMS) and 1-hydroxy ethylidene-1,1-diphosphonic acid(HEDP).The results of X-ray photoelectron spectroscopy(XPS),Fourier transform infrared spectroscopy(FTIR),potentiodynamic polarization scan,electrochemical impedance spectroscopy(EIS) and neutral salt spray(NSS) tests indicated that the major structure of the prepared silane-phosphonic acid composite passivation coating consisted mainly of Si—O—Si and Si—O—P bonds.The area of white rust was not more than 5% of the total panal after 120 h NSS test,which could be compared favourably with the chromate colour passivation coating.However,the corrosion reaction on the anode of the silane-phosphonic acid composite passivation …

Study On Preparing Technology And Corrosion Resistance Of Ti/Zr Based Chromium-Free Chemical Conversion Coating On Zinc Electroplating Layer, Yong Guan, Jian-Guo Liu, Chuan-Wei Yan

Journal of Electrochemistry

In this paper,we obtained environmental-friendly chromium-free chemical conversion coating on the non-cyanide alkaline zinc electroplating layer by employing the optimized Ti/Zr based conversion technique.At the same time,the performances of the Ti/Zr based conversion coating were compared with chromate colour passivation coating.The corrosion resistances of the conversion coatings were investigated by using neutral salt spray(NSS) test,potentiodynamic polarization and electrochemical impedance spectroscopy(EIS).The results showed that the white rust appeared after 96 hours when the NSS test was performed on the Ti/Zr based conversion coating,which was close to the corrosion resistance rating of chromate colour passivation coating.Compared with the chromate passivation coating,the Ti/Zr …

Coated Steel Rebar For Enhanced Concrete-Steel Bond Strength And Corrosion Resistance, Genda Chen, Jeffery S. Volz, Richard K. Brow, Dongming Yan, Signo Tadeu Dos Reis, Chenglin Wu, Fujian Tang, Charles R. Werner, Xing Tao

Civil, Architectural and Environmental Engineering Faculty Research & Creative Works

This report summarizes the findings and recommendations on the use of enamel coating in reinforced concrete structures both for bond strength and corrosion resistance of steel rebar. Extensive laboratory tests were conducted to characterize the properties of one- and two-layer enamel coatings. Pseudostatic tests were performed with pullout, beam and column specimens to characterize mechanical properties and develop design equations for the development length of steel rebar in lap splice and anchorage areas. The splice length equation was validated with the testing of large-scale columns under cyclic loading. For corrosion properties, ponding, salt spray, accelerated corrosion, potentiodynamic and electrochemical impedance …

Multi-Component Boron Coatings On Low Carbon Steel Aisi 1018, Naruemon Suwattananont

Dissertations

Boronizing and metalizing are thermo-chemical surface hardening treatments in which boron and metal atoms diffuse into the metal substrate forming metallic boride layers, providing complex properties of B-Me-Fe system.

To study multi-component boron coatings on low carbon steel AISI 1018, the simultaneous powder pack method of boronizing and metalizing was selected to perform the coatings. One B-Fe system and eight boron-metal (B-Me-Fe) systems from transition metals group IVB (Ti, Zr, Hf), group VB (Nb, Ta), and group VIB (Cr, Mo, W) were studied. The system specimens were thermo-chemically treated at 950°C for 4 hours in a crucible containing powder mixture …