An Investigation Of Initially Delaminated Composite Sandwich With Delamination Arrest Mechanism Under Buckling Loading, Tony D. Tran

Master's Theses

This thesis involves the development of a fiberglass-foam composite sandwich structure with the introduction of delamination arrestment keys; therefore, a study of an initially delaminated composite sandwich structure was the experimental analysis on multiple configurations in how the arrestment keys are placed.

The first part of this thesis research was to the experimental design and manufacturing of the composite sandwich plates. These plates were later cut down to the specific test dimensions and manufacturing processes for the composite sandwich plates and test specimens were created. The composite sandwich plates were manufactured using a vacuum resin infusion process. The dimensions of …

Design, Fabrication, Structural Testing, And Numerical Analysis Of A Small Scale Composite Wing, Jacob David Gaunt, Juan Carlos Flores, Vincent Andrew Perry

Aerospace Engineering

A small scale composite wing based on a design found on an experimental aircraft was designed, constructed, and tested dynamically and statically. The wing was constructed similarly to an experimental aircraft wing. The performed static test was intended to produce pure bending. Strain gages were used to measure strains on the wing structure. The strains were converted to stresses to aid in analysis. The static test results suggested that the wing was actually under torsion. Four structural modes were found from the static test. A finite element analysis model was made to compare experimental results to numerical analytical results. The …

Performance Of Sulfur-Super Conductive Carbon Black Composite In Electrolyte Mixed With Room Temperature Ionic Liquid, Bo Zhang, Si-Ting Chen, Xue-Ping Gao

Journal of Electrochemistry

The sulfur-super conductive carbon black composite was prepared as cathode material of lithium/sulfur battery.The composite was characterized by scanning electron microscopy(SEM),X-ray diffraction(XRD),and electrochemical impedance spectroscopy(EIS).The sulfur composite shows a high discharge capacity and a good cycle performance in electrolyte mixed with 50% of room temperature ionic liquid.In particular,the discharge capacity of the composite was stabilized at 483.6 mAh/g after 50 cycles.