The Study Of Corrosion On Additive-Manufactured Metals., Braydan Daniels

Electronic Theses and Dissertations

The purpose of this study was to investigate and compare the corrosion mechanisms between wrought and additive-manufactured (3D-printed) copper and stainless steel. The experimental procedure consisted of measuring the open circuit potential, electrochemical impedance spectroscopy, linear sweep voltammetry, Tafel analysis, surface topology, and scanning electron microscopy for each metal within salt water, tap water, sulfuric acid, and synthetic body fluid (excluding copper in synthetic body fluid).

Overall, printed stainless steel was more corrosion-resistant than wrought stainless steel in tap water and synthetic body fluid based on OCP, LSV, and surface topology results. Additionally, printed copper was more corrosion-resistant than wrought …

Use Of Electrochemical Techniques And Statistical Analysis To Investigate The Pitting Probability Of Copper, Sina Matin

Electronic Thesis and Dissertation Repository

The development of a safe permanent disposal plan is essential for the long-term disposal of used fuel bundles. Nuclear Waste Management Organization (NWMO) has been investigating the deep geologic disposal of nuclear waste which offers the optimum passive safety system with a negligible probability of release of radionuclides into the environment.

The proposed used fuel containers (UFC) for the permanent disposal of high-level nuclear waste in Canada is comprised of a carbon steel vessel coated with a 3 mm corrosion-resistant copper layer deposited using a combination of electrodeposition and cold spray deposition. Although copper is often considered to be thermodynamically …

Intergranular And Pitting Corrosion Mechanisms Of Sensitized Aluminum Alloy Aa5083, Clayton Egleston

Williams Honors College, Honors Research Projects

The motivation and objectives of this project is to examine the mechanisms of intergranular corrosion (IGC) and pitting corrosion of sensitized AA5083. In this regard, different characterization techniques were used, including optical analysis of microstructure, cyclic potentiodynamic polarization with Tafel fitting, electrochemical impedance spectroscopy with electrical equivalent circuit (EEC) fitting, and potentiostatic current transient monitoring. The transition from IGC to pitting corrosion occurs when the grain boundaries become saturated with the β-phase (Mg₂Al₃). It was found that AA5083 becomes more vulnerable to pitting corrosion as the degree of sensitization increases.