Microstructural Investigation Of Vintage Pipeline Steels Highly Susceptible To Stress Corrosion Cracking, Monica Adriana Torres
Microstructural Investigation Of Vintage Pipeline Steels Highly Susceptible To Stress Corrosion Cracking, Monica Adriana Torres
Open Access Theses & Dissertations
The use of pipelines for the transmission of gas offers not only efficiency, but a number of economic advantages. Nevertheless, pipelines are subject to aggressive operating conditions and environments which can lead to in-service degradation [1] and thus to failures. These failures can have catastrophic consequences, such as environmental damage and loss of life [2]. One of the most dangerous threats to pipeline integrity is stress corrosion cracking (SCC). Despite the substantial progress that has been achieved in the field, due to the complex nature of this phenomenon there is still not a complete understanding of this form of external …