Structural Properties And Crystallization Of Sodium Tellurite Glasses, Kresimir Furic, Masa Rajic-Linaric, C. S. Ray, A. Šantić, Andrea Moguš-Milanković, D. E. Day
Structural Properties And Crystallization Of Sodium Tellurite Glasses, Kresimir Furic, Masa Rajic-Linaric, C. S. Ray, A. Šantić, Andrea Moguš-Milanković, D. E. Day
Materials Science and Engineering Faculty Research & Creative Works
The structural properties and crystallization behaviour of xNa2O-(100-x)TeO2 (0 <= x <= 33.3, x-% mole fraction) glasses have been investigated by Raman spectroscopy, X-ray diffraction (XRD) and differential scanning calorimetry (DSC). The Raman spectra of glasses show systematic changes in structural units, from TeO4 trigonal bypiramids (tbps) to TeO3 trigonal pyramids (tps) with increasing Na2O content in glass. These structural changes are result of Te-eqOax-Te disruption and the formation of non-bridging oxygens (NBOs) in glass network. when heated at 623 K for 10 h glasses crystallized to different phases: alpha-TeO2, Na2Te4O9 and a new crystalline phase which is believed to be a polymorph of Na2Te2O5.
Processing And Characterization Of Samarium And Manganese Modified Lead Titanate Thin Film, Chen-Lung Fan, Wayne Huebner
Processing And Characterization Of Samarium And Manganese Modified Lead Titanate Thin Film, Chen-Lung Fan, Wayne Huebner
Materials Science and Engineering Faculty Research & Creative Works
Samarium and manganese modified lead titanate thin films were fabricated by spin-coating an amorphous citrate precursor. These films transformed into an oxide film upon heat treatment at 400 degrees Celcius or above. Relatively large area and crack-free thin films could be obtained by this process both easily and inexpensively. The rheological behavior of the precursor solution, as well as its thermal decomposition and phase development were studied by means of DSC/TGA and XRD. The thickness and grain size of the oxide film were examined by TEM and SEM.