The Effects Of Heat Treatment On Area Percent Porosity And Corrosion Behavior Of High-Nickel Thermal Spray Coatings, Travis Crowe, Alec Guraydin
The Effects Of Heat Treatment On Area Percent Porosity And Corrosion Behavior Of High-Nickel Thermal Spray Coatings, Travis Crowe, Alec Guraydin
Materials Engineering
Samples of two Thermal Spray Coating (TSC) alloys on a low carbon steel substrate were obtained: alloy C276 and Nicko-Shield 200. Specimens of each alloy were subjected to heat treatments at temperatures at 1100° for 60 minutes and 1200° for 10 minutes, with some specimens left in the as-sprayed condition. Three replicates were prepared for each condition. Thin 1” strips were cut using a diamond wafering blade for porosity measurements and 2” x 1” specimens were cut for corrosion testing using a SiC abrasive saw. The porosity specimens were mounted in acrylic resin, polished, and examined using SEM. From these …
The Effects Of Colorant Oxides And Firing Rate On The Nucleation And Growth Of Zinc Silicate Crystals In Crystalline Glazes, Nicolas Coffey
The Effects Of Colorant Oxides And Firing Rate On The Nucleation And Growth Of Zinc Silicate Crystals In Crystalline Glazes, Nicolas Coffey
Materials Engineering
This study looked at the effects of colorant oxides and firing rate on the nucleation and growth of crystals in zinc-based crystalline glazes. One weight percent of iron and copper oxide powders were mixed separately with a zinc-based crystalline glaze. The uncolored glaze along with both colored glazes were applied to test tiles and fired. Two different firing schedules were used with different ramp up firing rates of 165°C/hr (slow) and 205°C/hr (fast). X-ray diffraction (XRD) analysis found both zinc oxide and silica oxide in the raw glaze, which are the main components in the formation of zinc silicate. XRD …