Interactive Physics And Characteristics Of Photons And Photoelectrons In Hyperbranched Zinc Oxide Nanostructures, Garrett Edward Torix

Graduate Theses and Dissertations

As is commonly known, the world is full of technological wonders, where a multitude of electronic devices and instruments continuously help push the boundaries of scientific knowledge and discovery. These new devices and instruments of science must be utilized at peak efficiency in order to benefit humanity with the most advanced scientific knowledge. In order to attain this level of efficiency, the materials which make up these electronics, or possibly more important, the fundamental characteristics of these materials, must be fully understood. The following research attempted to uncover the properties and characteristics of a selected family of materials. Herein, zinc …

Zinc Oxide Nanorod Based Ultraviolet Detectors With Wheatstone Bridge Design, Arun Vasudevan

Graduate Theses and Dissertations

This research work, for the first time, investigated metal semiconductor-metal (MSM) zine oxide (ZnO) nanorod based ultra-violet (UV) detectors having a Wheatstone bridge design with a high

responsivity at room temperature and above, as well as a responsivity that was largely independent of the change in ambient conditions. The ZnO nanorods which acted as the sensing element of the detector were grown by a chemical growth technique. Studies were conducted to determine the effects on ZnO nanorod properties by varying the concentration of the chemicals used for the rod growth. These studies showed how the rod diameter and the deposition …

Synthesis Of Zinc Oxide Nanorods And Use In Biosensor Applications, Anishkumar Manoharan

Graduate Theses and Dissertations

The main aim of this research was to develop a nanorod based biosensor for biomedical applications. In this project I use zinc oxide nanorods as the bio-material for biosensor. I fabricated these nanorods using a solution-based technique. Initially I coated a zinc oxide seed layer as the base. This seed layer was then annealed at 350 degrees for almost 1 hour. As a next step, interdigitated electrodes were fabricated on the top of the seed layer using a lift off process. The zinc oxide nanorods were then grown at 90 degrees for almost 4 hours along the electrodes. In this …