Mechanical Properties Of Boride Based Ceramics, Alec Murchie

Doctoral Dissertations

“This research focuses on the elevated mechanical properties of diboride based materials at room and elevated temperatures. These materials include a ZrB₂ ceramic, a ZrB₂-WC-SiC ceramic, and a (Hf,Mo,Nb,Ta,W,Zr)B₂ high entropy boride (HEB). The room temperature flexural strength for the ZrB₂ ceramic was 447 MPa and the fracture toughness was 2.3 MPa·m^1/2. The strength decreased to 196 MPa at 1800°C, and then increased to 360 MPa at 2300°C. The fracture toughness increased to 3.1 MPa·m^1/2 at 2200°C. The strength up to 1800°C was likely controlled by a combination of effects: surface damage …

Synthesis And Applications Of Ceramic (Silicon Carbide And Silicon Nitride), Metallic (Cobalt(0)) And Polymeric (Polyurethane) Aerogels, Parwani M. Rewatkar

Doctoral Dissertations

"A new method has been demonstrated for the synthesis of monolithic ceramic and purely metallic aerogels from xerogel powder compacts, and the use of polyurethane aerogels based on cyclodextrins as efficient desiccants.

I. Highly porous ( > 80%) monolithic SiC and Si₃N₄, aerogels were prepared from compressed compacts of polyurea-crosslinked silica xerogel powders. The process is time efficient as solvent-exchange through powders is fast, and energy efficient as it bypasses drying with supercritical fluids. The final ceramic objects were chemically pure, sturdy, with compressive moduli at 37 ±7 MPa and 59 ± 7 MPa, and thermal conductivities …