Effect Of Tig Welding Parameters On Strain-Age Cracking In Joining Nickel-Based Superalloy, Gtd-111 With Inconel 625, Athittaya Athiroj, Panyawat Wangyao

Journal of Metals, Materials and Minerals

Excellent mechanical properties at high temperature of nickel-based superalloys brought them to extensive application in severe operating conditions. However, the great mechanical properties deteriorate after long-term exposure to high temperature and it frequently causes failure of the component e.g. cracking. TIG welding is considered as an economical way to refurbish the minor damage component as replacement with new one is costly due to high material cost and complexity in manufacturing processes. Unfortunately, heat from welding that applies to the component may create new cracks during and after process from liquation and strain-age cracking. This phenomena is problem especially in precipitation-hardened …