Design For Additive Manufacturing, Michael Charonnat, Leonardo Franco-Muñoz, Sam Noble, J.P. Purdom
Design For Additive Manufacturing, Michael Charonnat, Leonardo Franco-Muñoz, Sam Noble, J.P. Purdom
Mechanical Engineering
This document outlines the critical design details and timeline for the Design for Additive Manufacturing Senior Project sponsored by Solar Turbines, Inc. The scope of this project encompasses the redesign of two of Solar Turbine’s cast parts for metal additive manufacturing in order to minimize lead time, cost, and weight. With the overall objective of performing in-depth analysis exploring affordability & feasibility, this redesign process will aid Solar Turbines in expanding their knowledge of Design for Additive Manufacturing principles and enable them to further incorporate the use of additive manufacturing into their production processes. The first part that the team …
Evaluation Of Tensile Properties For Selective Laser Melted 316l Stainless Steel And The Influence Of Inherent Process Features, Paul Swartz
Master's Theses
Optimal print parameters for additively manufacturing 316L stainless steel using selective laser melting (SLM) at Cal Poly had previously been identified. In order to further support the viability of the current settings, tensile material characteristics were needed. Furthermore, reliable performance of the as-printed material had to be demonstrated. Any influence on the static performance of parts in the as-printed condition inherent to the SLM manufacturing process itself needed to be identified. Tensile testing was conducted to determine the properties of material in the as-printed condition. So as to have confidence in the experimental results, other investigations were also conducted to …
Characterization Of Laser Deposited Ti-6al-4v To Nb Gradient Alloys, Clincy Cheung
Characterization Of Laser Deposited Ti-6al-4v To Nb Gradient Alloys, Clincy Cheung
Materials Engineering
An alloy was fabricated with Ti-6Al-4V and Nb powder using laser deposition (LD) to form a compositional gradient. The gradient was deposited, starting with Ti-6Al-4V powder, onto a forged Ti-6Al-4V substrate in an Argon environment. Niobium (Nb) composition increased by 4-at.% with each layer deposited until the composition reached 100-at.% Nb. This process yielded steep thermal gradients and affected the microstructure and mechanical properties across the compositional gradient. To observe the microstructural changes in the alloy, an etched gradient was viewed with optical microscopy at 1000x, where the grain structure was observed to be an acicular α phase at 100-at.% …