Pressureless Sintering Of Zirconium Diboride With Carbon And Boron Carbide Nanopowder, Eric W. Neuman, Gregory E. Hilmas, William Fahrenholtz

Materials Science and Engineering Faculty Research & Creative Works

Zirconium diboride ceramics with and without carbon and boron carbide nano powder additives were prepared by ball milling with ZrB2 grinding media and pressureless sintering. Additions of up to 1 wt% nano-B4C and 0.5 wt% C were made to the ZrB2 powder. The materials were then sintered between 1800 and 2300 °C for between 90 and 360 min in an Ar/10H2 atmosphere. After sintering at 2200 °C for 90 min, densities ranged from 88.3 to 90.7% for the ZrB2 with 0–1.0% nano-B4C addition. Carbon additions of 0.5 wt% and nano-B4C additions from 0 to 1.0 wt% resulted in densities ranging …