Elevated Temperature Effects On The Mechanical Properties Of Age Hardened 6xxx Series Aluminum Alloy Extrusions, Rachael Donovan, Rose Fortune, Robert Trout
Elevated Temperature Effects On The Mechanical Properties Of Age Hardened 6xxx Series Aluminum Alloy Extrusions, Rachael Donovan, Rose Fortune, Robert Trout
Materials Engineering
The purpose of this project is to determine if over-aging of aluminum causes the yield or tensile strength to fall below the minimum strength values set by the aluminum industry. Extruded aluminum alloys, 6061-T6, 6063-T6, and two proprietary alloys, HS6X-T6 and RX82-T6, were exposed to reheating treatments at extended times and temperatures. The three temperatures were 350°F, 390°F, and 425°F. The times of reheat increased logarithmically from 30 minutes to 64 hours. The samples were tensile tested to determine the tensile strength and yield strength. Statistical methods helped model the behavior of yield and tensile strength as a function of …
Effect Of Time Delay Between Etching And Adhesive Bonding (“Outlife” Time) On Lap-Shear Strength Of Aluminum Alloys Using Environmentally-Friendly P2 Etch, Josh Barkhimer, Matthew Erich, Gokul Nair
Effect Of Time Delay Between Etching And Adhesive Bonding (“Outlife” Time) On Lap-Shear Strength Of Aluminum Alloys Using Environmentally-Friendly P2 Etch, Josh Barkhimer, Matthew Erich, Gokul Nair
Materials Engineering
Raytheon Company currently uses a Forest Products Laboratory (FPL) paste etchant for preparing aluminum surfaces for adhesive bonding, and FPL is a source of hazardous hexavalent chromium. The goal of this study was to evaluate a less-toxic P2 paste etchant as a possible replacement. Coupons of 2024-T3, 6061-T6, and 7075-T6 grades of aluminum alloy were solvent-degreased, abrasively cleaned, and etched at room temperature using P2 paste following a strict protocol adopted from Raytheon. Coupons were then left exposed to air for assigned time intervals (or “outlife” times) of 0, 1, 4, 8, 16, and 63 or 72 hours. The aluminum …