The Study Of Corrosion On Additive-Manufactured Metals., Braydan Daniels

Electronic Theses and Dissertations

The purpose of this study was to investigate and compare the corrosion mechanisms between wrought and additive-manufactured (3D-printed) copper and stainless steel. The experimental procedure consisted of measuring the open circuit potential, electrochemical impedance spectroscopy, linear sweep voltammetry, Tafel analysis, surface topology, and scanning electron microscopy for each metal within salt water, tap water, sulfuric acid, and synthetic body fluid (excluding copper in synthetic body fluid).

Overall, printed stainless steel was more corrosion-resistant than wrought stainless steel in tap water and synthetic body fluid based on OCP, LSV, and surface topology results. Additionally, printed copper was more corrosion-resistant than wrought …

Near-Ir Laser Ablation Of Simulated Radiologically Contaminated Oxides On Carbon Steel Feeder Pipes, Thao Viet Do

Electronic Thesis and Dissertation Repository

As nuclear power plants age and retire from service, many countries face significant challenges concerning the safe long-term storage and disposal of large volumes of low and intermediate level radioactive wastes (L&ILW). The volumes of metallic waste are of particular concern, as when metal corrodes it produces hydrogen that could lead to pressure build-up in interim storage and disposal. In Canada, a significant fraction of the metallic wastes for Canada Deuterium Uranium (CANDU) nuclear reactors are out-of-core reactor components, such as carbon steel (CS) feeder pipes. The radioactive contamination is expected to be largely confined to the surface oxide layers …

Numerical Study Of Oxidation In Stainless Steel Alloy Ep-823 By Liquid Lead-Bismuth Eutectic, Rajyalakshmi Palaparty

UNLV Theses, Dissertations, Professional Papers, and Capstones

The oxidation of stainless steel is influenced by the presence of oxygen in the surrounding medium; the oxygen reacts with the alloy to form an oxide. In certain environments, such as nuclear reactor coolant systems, minimal oxidation of the stainless steel containment functions as a protective shield from corrosive coolants such as liquid lead-bismuth eutectic.

In the current study, this minimal oxidation is evaluated for a system in which corrosion-resistant stainless steel alloy EP-823 is subject to an environment of flowing oxygenated liquid lead-bismuth eutectic at a temperature of 743 K, whereby the thickness of the forming oxide layer is …

Microstructural Investigation Of Vintage Pipeline Steels Highly Susceptible To Stress Corrosion Cracking, Monica Adriana Torres

Open Access Theses & Dissertations

The use of pipelines for the transmission of gas offers not only efficiency, but a number of economic advantages. Nevertheless, pipelines are subject to aggressive operating conditions and environments which can lead to in-service degradation [1] and thus to failures. These failures can have catastrophic consequences, such as environmental damage and loss of life [2]. One of the most dangerous threats to pipeline integrity is stress corrosion cracking (SCC). Despite the substantial progress that has been achieved in the field, due to the complex nature of this phenomenon there is still not a complete understanding of this form of external …

Galvanic Corrosion On Monel K-500 And 1018 Carbon Steel Couple, John K. Nnyanzi

Williams Honors College, Honors Research Projects

The purpose of this research project was to evaluate galvanic damage on 1018 Carbon Steel coupled to Monel K-500 at varying rotation speeds on a rotating cylinder electrode in an aerated solution of ASTM artificial seawater. The work in this project is and attempt to study corrosion behavior for a Monel fastener coupled to a Carbon Steel plate. Polarization curves of each material at different rotation speeds were created to predict the corrosion behavior for a galvanic couple of Carbon Steel and Monel. The Potentiodynamic sweeps predict an increase in the corrosion current density for the galvanic couple when then …

The Examination Of Stress Corrosion Cracking In High Strength Carbon Steel Through Combined Mechanical-Electrochemical Testing, Jacob Sines

Williams Honors College, Honors Research Projects

Through the analysis of materials and environments seen in industry a better understanding of the fundamentals behind degradation mechanisms can be observed. The scope of this project was to better understand the fundamentals behind the degradation of high strength pipeline steels in a lab setting to simulate an environment seen in industry. Specifically the degradation mechanisms of high and nearly neutral pH stress corrosion cracking were examined in environments that simulated oil and gas pipelines buried in soil. Experimentation was carried out utilizing X65 carbon steel specimen, a Gamry potentiostat, a CORTEST proof ring, a CORTEST slow strain rate machine, …

The Effects Of Uncommon Silicides On The Oxidation Of Alloys From The Nb-Cr-Si System, Daniel Brendan Voglewede

Open Access Theses & Dissertations

Niobium based alloys are being tapped as potential successors to current nickel base superalloys in high temperature applications. In the aerospace industry, high temperature materials are constantly being pushed to higher temperature regimes in order to improve engine efficiency however current superalloys cannot be pushed further due to melting temperature limitations. Niobium, being a refractory metal, can withstand much higher temperatures than nickel however its oxidation properties are woefully inadequate.

The purpose of this study is to ascertain whether increased silicon additions can improve niobium oxidation properties by: forming ternary silicides with better oxidation properties and by preventing the formation …