Structure And Magnetism Of Nanocrystalline Exchange-Coupled (Ni₀.₆₇Co₀.₂₅Fe₀.₀₈)₈₉₋ₓzr₇B₄Cuₓ (X=0,1) Films, S. Joshi, S. D. Yoon, A. Yang, N. X. Sun, C. Vittoria, V. G. Harris, R. Goswami, M. Willard, N. Shi
Structure And Magnetism Of Nanocrystalline Exchange-Coupled (Ni₀.₆₇Co₀.₂₅Fe₀.₀₈)₈₉₋ₓzr₇B₄Cuₓ (X=0,1) Films, S. Joshi, S. D. Yoon, A. Yang, N. X. Sun, C. Vittoria, V. G. Harris, R. Goswami, M. Willard, N. Shi
Nian X. Sun
Structural and magnetic characterizations of nanocrystalline films of (Ni₀.₆₇Co₀.₂₅Fe₀.₀₈)₈₉₋ₓZr₇B₄Cuₓ (x=0,1) alloys are reported. The films were grown on quartz substrates using pulsed laser deposition from homogeneous targets of the above compositions at substrate temperatures ranging from ambient to 600°C. Structural properties were measured by x-ray diffraction, atomic force microscopy, and transmission electron microscopy, whereas the magnetic properties were measured by vibrating sample magnetometry and ferromagnetic resonance. The resulting films exist as a two phase alloy with face-centered-cubic metallic grains suspended in an amorphous matrix. For both the x=1 and x=0 alloys, the softest magnetic properties (coercivity Hc < 0.5 Oe, 4πMs …
Microwave, Magnetic, And Structural Properties Of Nanocrystalline Exchange-Coupled Ni₁₁Co₁₁Fe₆₆Zr₇B₄Cu₁ Films For High Frequency Applications, S. D. Yoon, A. K. Baraskar, A. Geiler, A. Yang, C. Pettiford, N. X. Sun, R. Goswami, M. A. Willard, C. Vittoria, V. G. Harris
Microwave, Magnetic, And Structural Properties Of Nanocrystalline Exchange-Coupled Ni₁₁Co₁₁Fe₆₆Zr₇B₄Cu₁ Films For High Frequency Applications, S. D. Yoon, A. K. Baraskar, A. Geiler, A. Yang, C. Pettiford, N. X. Sun, R. Goswami, M. A. Willard, C. Vittoria, V. G. Harris
Nian X. Sun
Nanocrystalline structured films of the alloy Ni₁₁Co₁₁Fe₆₆Zr₇B₄Cu₁ were deposited by pulsed laser ablation deposition onto fused quartz substrates. A substrate temperature of 300°C was found to produce films consisting of body-centered-cubic (bcc) metallic grains suspended in an amorphous matrix. The bcc grain size ranged from 5 - 8 nm for substrate temperatures up to 300°C. Measured values of coercivity were consistently below 4 Oe for films having a saturation magnetization, as 4π Ms, of ∽16 kG with in- plane uniaxial anisotropy fields of 25 to 30 Oe. The ferromagnetic resonance peak- to- peak derivative linewidth was measured to be 34 …